多道环氧涂层在NaCl溶液中的电化学阻抗谱

谢德明;胡吉明;童少平

浙江大学

Electrochemical impedance spectroscopy of multi-layer epoxy coatings in NaCl solution

;;

浙江大学

引用本文:

谢德明; 胡吉明; 童少平 . 多道环氧涂层在NaCl溶液中的电化学阻抗谱[J]. 材料研究学报, 2004, 18(1): 96-96.

全文: PDF(1404 KB)

摘要: 采用电化学阻抗谱（EIS）方法研究了环氧涂层的厚度与涂装道数对水传输行为的影响。水分子在具有良好阻挡作用的多道环氧涂层的初始阶段的传输符合Fick定律，并求得了水在涂层中的表观扩散系数值，与之相应的干环氧涂层的介电常数ed为4.2。涂层越厚，涂装道数越多，介质在涂层中的传输越困难，涂层的抗渗透性能越好。多道环氧涂层的涂层电容－时间曲线类似于理想情况下单道涂层在水溶液中的涂层电容与浸泡时间的关系曲线。

关键词 ：材料失效与保护, 环氧涂层, 电化学阻抗谱

Abstract：The diffusion behavior of water through epoxy coatings as a function of the film thickness and the painting number was studied by electrochemical impedance spectroscopy (EIS) techniques. The experimental results showed that, in 3.5 wt.% NaCl solution, the diffusion process of water through multi-layer organic coatings with good barrier performance followed the ideal Fick's law in the initial period. The corresponding diffusion coefficient was also derived and the dielectric constant of the dry coatings (ed) was found to be 4.2. The resistance to medium permeation of the coatings increased with increasing of film thickness and the number of coats.

Key words： materials failure and protection epoxy coatings electrochemical impedance spectroscopy water uptake

收稿日期: 2004-04-01

ZTFLH:

TB304

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	谢德明
	胡吉明
	童少平
44.8K

链接本文:

https://www.cjmr.org/CN/Y2004/V18/I1/96

1 V.B.Miskovic-Stankovic, D.M.Drazic, M.J.Teodorovic, Corrosion Science, 37, 241(1995)
2 L.De.Rosa, T.Monetta, D.B.Mitton, F.Bellucci, J.Electrochem.Soc, 145, 3830(1998)
3 HU Jiming(胡吉明), ZHANG Jianqing(张鉴清), XIE Deming(谢德明), CAO Chu'nan(曹楚南), Acta Physico-Chimica Sinica (物理化学学报), 19, 144(2003)
4 HU Jiming(胡吉明), ZHANG Jianqing(张鉴清), CAO Chu'nan(曹楚南), Acta metallurgica(金属学报), 39, 544(2003)
5 W.Meuleman, R.Vandenkerckhove, E.Temmerman, Materials Science Forum, 289-292, 383(1998)
6 V.B.Miskovic-Stankovic, J.B.Zotovic, M.D.Maksimovic, Materials Science Forum, 289-292, 327(1998)
7 K.M.Yin, H.Z.Wu, Surface and Coatings Technology, 106, 167(1998)
8 F.Bellucci, L.Nicodemo, Corrosion, 49, 235(1993)
9 N.L.Thomas, Progress in Organic Coatings, 19, 101(1991)
10 G.K.Vanderwel, O.C.G.Adan, Progress in Organic Coatings, 37, 1(1999)
11 H.Leidheiser Jr, Progress in Organic Coatings, 7, 79(1979)
12 H.Leidheiser Jr, Journal of Coatings Technology, 63(802) , 21(1991)
13 F.Mansfeld, S.Kim, S.Lin, Journal of Coatings Technology, 61(774) , 33(1989)
14 H.Xiao, F.Mansfeld, Journal of the Electrochemical Society, 141(9) , 2332(1994)
15 G.Cerisola, Material Chemistry, 7(2) , 241(1982)
16 C.Perez, A.Collazo, M.Izquierdo, P.Merino, X.R.Novoa, Progress in Organic Coatings, 36, 102(1999)
17 C.Perez, A.Collazo, M.Izquierdo, P.Merino, X.R.Novoa, Progress in Organic Coatings, 37, 169(1999)
18 P.L.Bonora, F.Deflorian, L.Fedrizzi, Electrochimica Acta, 41, 1073(1996)
19 R.I.Trezona, I.M.Hutchings, Progress in Organic Coatings, 41, 85(2001)
20 V.Guillaumin, G.Mankowski, Corrosion Science, 41, 421(1999)
21 L.Lavaert, M.De Cock, M.Moors, E.Wettinck, Progress in Organic Coatings, 38, 213(2000)
22 D.H.V.D.Weijde, E.P.M.V.Westing, J.H.W.D.Wit, Materials Science Forum, 289-292, 237(1998)
23 T.Monetta, F.Bellucci, L.Nicodemo, L.Nicolais, Progress in Organic Coatings, 21, 353(1993)
24 B.N.Popov, M.A.Alwohaibi, R.E.White, J.Electrochem.Soc, 140, 947(1993)
25 J.R.Scully, J.Electrochem.Soc, 136, 979(1989)
26 V.B.Miskovic-Stankovic, M.R.Stanic, D.M.Drazic, Progress in Organic Coatings, 36, 241(1999)

[1]	高巍, 刘江南, 魏敬鹏, 要玉宏, 杨巍. TC4钛合金表面氧化亚铜掺杂微弧氧化层的结构和性能[J]. 材料研究学报, 2022, 36(6): 409-415.
[2]	杨留洋, 谭卓伟, 李同跃, 张大磊, 邢少华, 鞠虹. 利用WBE及EIS测试技术对管道缺陷区动态冲刷腐蚀行为的研究[J]. 材料研究学报, 2022, 36(5): 381-391.
[3]	陈铮, 杨芳, 王成, 杜瑶, 卢壹梁, 朱圣龙, 王福会. 惰性无机填料比例和颗粒尺寸对纳米Al/Al₂O₃ 改性有机硅涂料抗高温氧化行为的影响[J]. 材料研究学报, 2022, 36(4): 271-277.
[4]	李玉峰, 张念飞, 刘丽爽, 赵甜甜, 高文博, 高晓辉. 含磷石墨烯的制备及复合涂层的耐蚀性能[J]. 材料研究学报, 2022, 36(12): 933-944.
[5]	陈艺文, 王成, 娄霞, 李定骏, 周科, 陈明辉, 王群昌, 朱圣龙, 王福会. 无机复合涂层对CB2铁素体耐热钢在650℃水蒸气中的防护[J]. 材料研究学报, 2021, 35(9): 675-681.
[6]	唐荣茂, 刘光明, 刘永强, 师超, 张帮彦, 田继红, 甘鸿禹. 用电化学噪声技术研究Q235钢在含氯盐模拟混凝土孔隙液中的腐蚀行为[J]. 材料研究学报, 2021, 35(7): 526-534.
[7]	张大磊, 魏恩泽, 荆赫, 杨留洋, 豆肖辉, 李同跃. 超级铁素体不锈钢表面超疏水结构的制备及其耐腐蚀性能[J]. 材料研究学报, 2021, 35(1): 7-16.
[8]	王冠一, 车欣, 张浩宇, 陈立佳. Al-5.4Zn-2.6Mg-1.4Cu合金板材的低周疲劳行为[J]. 材料研究学报, 2020, 34(9): 697-704.
[9]	黄安然, 张伟, 王学林, 尚成嘉, 范佳杰. 铁素体不锈钢在高温尿素环境中的腐蚀行为研究[J]. 材料研究学报, 2020, 34(9): 712-720.
[10]	公维炜, 杨丙坤, 陈云, 郝文魁, 王晓芳, 陈浩. 扫描电化学显微镜原位观察碳钢涂层缺陷处的交流腐蚀行为[J]. 材料研究学报, 2020, 34(7): 545-553.
[11]	郭铁明, 徐秀杰, 张延文, 宋志涛, 董志林, 金玉花. Q345q桥梁钢和Q345qNH耐候钢在模拟工业大气+除冰盐混合介质中的腐蚀行为[J]. 材料研究学报, 2020, 34(6): 434-442.
[12]	朱金阳, 谭成通, 暴飞虎, 许立宁. 一种新型含Al低Cr合金钢在模拟油田采出液环境下的CO₂腐蚀行为[J]. 材料研究学报, 2020, 34(6): 443-451.
[13]	梁新磊, 刘茜, 王刚, 王震宇, 韩恩厚, 王帅, 易祖耀, 李娜. 氧化石墨烯改性环氧隔热涂层的耐蚀和隔热性能研究[J]. 材料研究学报, 2020, 34(5): 345-352.
[14]	王志虎,张菊梅,白力静,张国君. 水热处理对AZ31镁合金微弧氧化陶瓷层组织结构及耐蚀性的影响[J]. 材料研究学报, 2020, 34(3): 183-190.
[15]	段体岗, 黄国胜, 马力, 彭文山, 张伟, 许立坤, 林志峰, 何华, 毕铁满. Q235/Ni-Co基自修复涂层的制备和耐蚀性能[J]. 材料研究学报, 2020, 34(10): 777-783.

Viewed

Full text

Abstract

Cited

Shared

Discussed