材料研究学报  2004, Vol. 18 Issue (1): 102-102

论文 本期目录 | 过刊浏览 |

喷射轧制钢/Al-Pb复合轴瓦带材的组织与性能

田冲;陈桂云;杨林;赵九洲;张永昌

中国科学院金属研究所

Microstructure and properties os steelAl-Pb composite bearing plate prepared by spray forming and rolling

;;;;

中国科学院金属研究所

田冲; 陈桂云; 杨林; 赵九洲; 张永昌 . 喷射轧制钢/Al-Pb复合轴瓦带材的组织与性能[J]. 材料研究学报, 2004, 18(1): 102-102.

摘要 参考文献 相关文章 Metrics 全文: PDF(2483 KB)   摘要: 采用喷射轧制工艺制备了钢/Al-8.5Pb-4Si-Cu-0.5Sn复合轴瓦带材，分析了所制备材料的组织及性能。结果表明，喷射轧制工艺制备的轴瓦合金Al-Si基体中具有均匀细小的Pb相粒子分布，经过50%变形量的轧制及320℃，5小时的后续退火处理，复合轴瓦带材的界面处发生了合金元素的扩散，形成了良好的冶金结合层，界面强度高，剪切强度可以达到72MPa，制备的轴瓦合金耐磨性能良好。 关键词 ： 复合材料,  钢/Al-Pb复合轴瓦带材,  喷射成形     Abstract：The spray forming and rolling process was used for the preparation of steel/Al-8.5Pb-4Si-Cu-0.5Sn (wt%) composite bearing strip. The microstructure and the mechanical properties of the spray formed steel / Al-Pb composite strip were analyzed. It shows that the microstructure of the spray formed Al-Pb layer consists of the Al-Si matrix and the homogeneously distributed refined Pb particles. After a rolling of 50% reduction and followed by annealing at 320℃ for 5 hours, the interfacial shearing strength between the spray formed Al-Pb layer and the steel strip is 72MPa. The high interfacial bonding strength is due to the formation of diffusion layer between the steel substrate and the spray formed Al-Pb alloy layer. The refined Pb particles improve the wear-resistant property of the bearing alloy. Key words： composite    steel/Al-Pb composite bearing strip    spray forming    interfacial bonding strength    wear-resist 收稿日期: 2003-01-13      ZTFLH:  TB331   服务 把本文推荐给朋友 加入引用管理器 E-mail Alert RSS 作者相关文章 田冲 陈桂云 杨林 赵九洲 张永昌 44.8K 链接本文: https://www.cjmr.org/CN/Y2004/V18/I1/102 1 J.Z.Zhao, L.Ratke, Modeling Simul.Sci.Eng., 6, 123(1998) 2 A.Sharma, T.V.Rajan, Wear, 197, 105(1996) 3 Collycar.John, The Chinese Journal of Nonferrous Metals(中国有色金属学报),3(4) , 88(1993) 4 S.Mohan, V.AgarWala, S.Ray, Wear, 140, 83(1990) 5 K.Lepper, M.James, J.Chashechkina, Wear, 203, 46(1997) 6 SUN Daren(孙大仁), LIU Yongbing(刘勇兵), AN Jian(安健), LU You(陆有), CAO Zhanyi(曹占义),The Chinese Journal of Nonferrous Metals(中国有色金属学报), 8(Supp1． 1) , 141(1998) 7 B.Prinz, A.Romero, In: Immiscible Liquid Metals and Organics, L.Ratke ed., (DGM-Informations gesellschaft, Oberursel, Germany, 1993) p.281 8 T.Berrenberg, In: Immiscible Liquid Metals and Organics, L.Ratke ed., (DGM-Informationsgesellschaft, Oberursel, Germany, 1993) p.299 9 Y.Ogita, Y.Ido, M.Sakamoto, Metallurgy of Powder Research, 2, 37(1991) 10 A.R.E.Singer, Metals and Materials, 4(6) , 246(1970) 11 P.S.Grant, Spray Forming, Prog.Mater.Sci., 39, 497(1995) 12 A.Updhyaya, N.S.Mishra, S.N.Ojha, Journal of Material Science, 32, 3227(1997) 13 LI Xiaoxue(李晓学), LIU Yong(刘勇), SUN Jiyue(孙继跃), CUI Hua(崔华), DUAN Xianjin(段先进), ZHANG Jishan(张济山), The Chinese Journal of Nonferrous Metals (中国有色金属学报), 9(Supp1． 1) , 106(1999) 14 YU Jiuming(于九明), YU Changsheng(于长生), ZHU Quan(朱泉), Journal of Northeastern University (Natural Science) (东北大学学报(自然科学版)), 16(5) , 491(1995) 15 ZHANG Caipei(张彩碚), CUI Jianzhong(崔建忠), Acta Metallurgica Sinica(金属学报), 35, 113(1998) 16 D.Pan, K.Gao, J.Yu, Materials Science and Technology, 5(9) , 934(1989) 17 ZHU Quan(朱泉), PAN Dawei(潘大炜), ZHANG Wenqi(张文奇), Steel Rolling(轧钢), 4, 19(1989) 18 S.N.Ojha, A.K.Tripathi, S.N.Singh, Powder Metallurgy Inter., 25(2) , 65(1993) [1] 潘新元, 蒋津, 任云飞, 刘莉, 李景辉, 张明亚. 热挤压钛/钢复合管的微观组织和性能[J]. 材料研究学报, 2023, 37(9): 713-720. [2] 刘继浩, 迟宏宵, 武会宾, 马党参, 周健, 徐辉霞. 喷射成形M3高速钢热处理过程中组织的演变和硬度偏低问题[J]. 材料研究学报, 2023, 37(8): 625-632. [3] 刘瑞峰, 仙运昌, 赵瑞, 周印梅, 王文先. 钛合金/不锈钢复合板的放电等离子烧结技术制备及其性能[J]. 材料研究学报, 2023, 37(8): 581-589. [4] 季雨辰, 刘树和, 张天宇, 查成. MXene在锂硫电池中应用的研究进展[J]. 材料研究学报, 2023, 37(7): 481-494. [5] 王伟, 解泽磊, 屈怡珅, 常文娟, 彭怡晴, 金杰, 王快社. Graphene/SiO2 纳米复合材料作为水基润滑添加剂的摩擦学性能[J]. 材料研究学报, 2023, 37(7): 543-553. [6] 张藤心, 王函, 郝亚斌, 张建岗, 孙新阳, 曾尤. 基于界面氢键结构的石墨烯/聚合物复合材料的阻尼性能[J]. 材料研究学报, 2023, 37(6): 401-407. [7] 邵萌萌, 陈招科, 熊翔, 曾毅, 王铎, 王徐辉. C/C-ZrC-SiC复合材料的Si2+ 离子辐照行为[J]. 材料研究学报, 2023, 37(6): 472-480. [8] 张锦中, 刘晓云, 杨健茂, 周剑锋, 查刘生. 温度响应性双面纳米纤维的制备和性能[J]. 材料研究学报, 2023, 37(4): 248-256. [9] 王刚, 杜雷雷, 缪自强, 钱凯成, 杜向博文, 邓泽婷, 李仁宏. 聚多巴胺改性碳纤维增强尼龙6复合材料的界面性能[J]. 材料研究学报, 2023, 37(3): 203-210. [10] 林师峰, 徐东安, 庄艳歆, 张海峰, 朱正旺. TiZr基非晶/TC21双层复合材料的制备和力学性能[J]. 材料研究学报, 2023, 37(3): 193-202. [11] 苗琪, 左孝青, 周芸, 王应武, 郭路, 王坦, 黄蓓. 304不锈钢纤维/ZL104铝合金复合泡沫的孔结构、力学、吸声性能及其机理[J]. 材料研究学报, 2023, 37(3): 175-183. [12] 张开银, 王秋玲, 向军. FeCo/SnO2 复合纳米纤维的制备及其吸波性能[J]. 材料研究学报, 2023, 37(2): 102-110. [13] 周聪, 昝宇宁, 王东, 王全兆, 肖伯律, 马宗义. (Al11La3+Al2O3)/Al复合材料的高温性能及其强化机制[J]. 材料研究学报, 2023, 37(2): 81-88. [14] 罗昱, 陈秋云, 薛丽红, 张五星, 严有为. 钠离子电池双层碳包覆Na3V2(PO4)3 正极材料的超声辅助溶液燃烧合成及其电化学性能[J]. 材料研究学报, 2023, 37(2): 129-135. [15] 刘志华, 岳远超, 丘一帆, 卜湘, 阳涛. g-C3N4/Ag/BiOBr复合材料的制备及其光催化还原硝酸盐氮[J]. 材料研究学报, 2023, 37(10): 781-790. Viewed Full text Abstract Cited   Shared      Discussed