材料研究学报  2013, Vol. 27 Issue (2): 219-224

研究报告 本期目录 | 过刊浏览 |

木质素基活性炭的制备和吸附特性*

田龙1, 2 马晓建1

1. 郑州大学 化工与能源学院 郑州 450001 2. 南阳师范学院 南阳 473061

Preparation and Adsorption Property of of Activated Carbon from Ligin

TIAN Long1,2 MA Xiaojian1**

1. College of Chemical Engineering and Energy, Zhengzhou University, Zhengzhou 450001; 2. Nanyang Normal University, Nanyang 473061

田龙 马晓建. 木质素基活性炭的制备和吸附特性*[J]. 材料研究学报, 2013, 27(2): 219-224.
. Preparation and Adsorption Property of of Activated Carbon from Ligin[J]. Chinese Journal of Materials Research, 2013, 27(2): 219-224.

摘要 参考文献 相关文章 Metrics 全文: PDF(747 KB)   摘要: 摘 要 用磷酸活化法制备木质素基活性炭, 研究了浸渍比、磷酸浓度、活化温度、活化时间对其吸附性能和得率的影响。结果表明, 随着浸渍比、磷酸浓度、活化温度、活化时间的增加, 活性炭的碘吸附值和亚甲基蓝吸附值均先升后降。适当提高这4个数值有助于木质素形成较多的微孔, 提高活性炭的吸附性能; 但超过一定程度时, 活性炭内部的部分微孔之间的孔壁变薄甚至被烧穿, 造成微孔扩大至中孔甚至大孔。同时, 磷酸与已生成的微孔结构的孔壁碳原子发生反应, 引起炭材料过度烧蚀, 使孔径变大, 导致活性炭的吸附性能降低。这种活性炭对苯酚的吸附符合Freundlich等温吸附方程, 吸附动力学符合Lagergren拟二级速率方程。 关键词 ： 无机非金属材料,  活性炭,  磷酸,  吸附     Abstract： Activated carbon from ligin was prepared by phosphate activation in this paper. The effects of 4 factors such as impregnation ratio, phosphate concentration, activation temperature and activation time on the adsorption properties of activated carbons and yield were investigaited. The results show activated carbon iodine adsorption value and methylene blue adsorption value increase at first and then decrease with the increase of impregnation ratio, phosphate concentration, activation temperature and activation time. The four factors contribute to the formation of more micropores, and improve activated carbon adsorption properties. However exceeding a certain level, the internal part of the micropores of the activated carbon between the bore wall thin even burn, resulting in the microporous expanded to the hole and even largeholes. At the same time, phosphate can react with the carbon atoms of a hole wall forming the microporous structure, causing the carbon material excessive ablation, the large pore size, so that the adsorption properties of the activated carbon is reduced. The equilibrium adsorption datum match Freundlich model well. The adsorptions of phenol by activated carbon resin are in accordance with Freundlich isotherm model, and the adsorption kinetics data fit well with the Lagergren pseudo-second order rate equation. Key words： inorganic nonmetallic materials    activated carbon    phosphate    adsorption      ZTFLH:  TQ424   服务 把本文推荐给朋友 加入引用管理器 E-mail Alert RSS 作者相关文章 44.8K 链接本文: https://www.cjmr.org/CN/      或      https://www.cjmr.org/CN/Y2013/V27/I2/219 1 CHEN Hongzhang, QIU Weihua, The crucial problems and recent advance on producing fuel alcohol by fermentation of straw, Progress in Chemistry, 19(7/8), 1116(2007) (陈洪章, 邱卫华, 秸秆发酵燃料乙醇关键问题及其进展, 化学进展, 19(7/8), 1116(2007)) 2 V. Fierro, V. Torne-Fernandez, D. Montane, A. Celzard, Study of the decomposition of kraft lignin impregnated with orthophosphoric acid, Thermochimica Acta, 433(6), 142(2005) 3 LIU Liheng, GU Min, XIAN Xuefu, YU Jiangtao, Effect of binders on ch4/n2 performances of granular activated carbons by pressure swing adsorption, Chinese Journal of Materials Research, 25(3), 249(2012) (刘立恒, 辜 敏, 鲜学福, 喻江涛, 粘结剂对颗粒活性炭PSA分离CH4/N2性能的影响, 材料研究学报, 25(3), 249(2012)) 4 LI Xuan, NI Wen, HUANG Jianyang, ZHANG Zheng, Influence of piezoelectric element on hydrogen adsorption of pt-supported activated carbon, Chinese Journal of Materials Research, 24(5), 551(2010) (李 轩, 倪 文, 黄建阳, 张 筝, 压电材料对含铂活性炭氢气吸附性能的影响, 材料研究学报, 24(5), 551(2010)) 5 E. Gonzalez-Serrano, T. Cordero, J. Rodriguez-Mirasol, Removal of water pollutants with activated carbons prepared from H3PO4 activation of lignin from kraft black liquors, Water Research, 38, 3043(2004) 6 J. M. V. Nabais, P. J. M. Carrott, M. M. L. R. Carrott, Preparation and modification of activated carbon fibres by microwave heating, Carbon, 42(7), 1315(2004) 7 A. S. OZCAN, B. ERDOM, Adsorption of acid blue 193 from aqueous solutions onto BTMA-hnntonite, Colloid Interface Sci, 280(1), 44(2004) 8 WANG Xiufang, ZHANG Huiping, XIAO Xinyan, CHEN Huanqin, Adsorption equilibrium and dynamics of phenol on bamboo charcoals, Journal of Functional Materials, 36(5), 746(2005) (王秀芳, 张会平, 肖新颜, 陈焕钦, 苯酚在竹炭上的吸附平衡和动力学研究, 功能材料, 36(5), 746(2005)) [1] 宋莉芳, 闫佳豪, 张佃康, 薛程, 夏慧芸, 牛艳辉. 碱金属掺杂MIL125的CO2 吸附性能[J]. 材料研究学报, 2023, 37(9): 649-654. [2] 邵鸿媚, 崔勇, 徐文迪, 张伟, 申晓毅, 翟玉春. 空心球形AlOOH的无模板水热制备和吸附性能[J]. 材料研究学报, 2023, 37(9): 675-684. [3] 任富彦, 欧阳二明. g-C3N4 改性Bi2O3 对盐酸四环素的光催化降解[J]. 材料研究学报, 2023, 37(8): 633-640. [4] 刘明珠, 樊娆, 张萧宇, 马泽元, 梁城洋, 曹颖, 耿仕通, 李玲. SnO2 作散射层的光阳极膜厚对量子点染料敏化太阳能电池光电性能的影响[J]. 材料研究学报, 2023, 37(7): 554-560. [5] 李延伟, 罗康, 姚金环. Ni(OH)2 负极材料的十二烷基硫酸钠辅助制备及其储锂性能[J]. 材料研究学报, 2023, 37(6): 453-462. [6] 余谟鑫, 张书海, 朱博文, 张晨, 王晓婷, 鲍佳敏, 邬翔. N掺杂生物炭的制备及其对Co2+ 的吸附性能[J]. 材料研究学报, 2023, 37(4): 291-300. [7] 朱明星, 戴中华. SrSc0.5Nb0.5O3 改性BNT基无铅陶瓷的储能特性研究[J]. 材料研究学报, 2023, 37(3): 228-234. [8] 刘志华, 岳远超, 丘一帆, 卜湘, 阳涛. g-C3N4/Ag/BiOBr复合材料的制备及其光催化还原硝酸盐氮[J]. 材料研究学报, 2023, 37(10): 781-790. [9] 周毅, 涂强, 米忠华. 制备方法对磷酸盐微晶玻璃结构和性能的影响[J]. 材料研究学报, 2023, 37(10): 739-746. [10] 谢锋, 郭建峰, 王海涛, 常娜. ZnO/CdS/Ag复合光催化剂的制备及其催化和抗菌性能[J]. 材料研究学报, 2023, 37(1): 10-20. [11] 余超, 邢广超, 吴郑敏, 董博, 丁军, 邸敬慧, 祝洪喜, 邓承继. 亚微米Al2O3 对重结晶碳化硅的作用机制[J]. 材料研究学报, 2022, 36(9): 679-686. [12] 方向明, 任帅, 容萍, 刘烁, 高世勇. 自供能Ag/SnSe纳米管红外探测器的制备和性能研究[J]. 材料研究学报, 2022, 36(8): 591-596. [13] 李福禄, 韩春淼, 高嘉望, 蒋健, 许卉, 李冰. 氧化石墨烯的变温发光[J]. 材料研究学报, 2022, 36(8): 597-601. [14] 杨琴, 王振, 房春娟, 王若迪, 高大航. 力学性能可控的CMC/AA/CB[8]/BET凝胶的制备及其吸附性[J]. 材料研究学报, 2022, 36(8): 628-634. [15] 朱晓东, 夏杨雯, 喻强, 杨代雄, 何莉莉, 冯威. Cu掺杂金红石型TiO2 的制备及其光催化性能[J]. 材料研究学报, 2022, 36(8): 635-640. Viewed Full text Abstract Cited   Shared      Discussed