材料研究学报  2005, Vol. 19 Issue (1): 1-7

论文 本期目录 | 过刊浏览 |

pH值对镁合金AM60疲劳寿命的影响

曾荣昌;韩恩厚;柯伟;刘路;徐永波

中国科学院金属研究所国家腐蚀与防护重点实验室

;;;;

中国科学院金属研究所国家腐蚀与防护重点实验室

曾荣昌; 韩恩厚; 柯伟; 刘路; 徐永波 . pH值对镁合金AM60疲劳寿命的影响[J]. 材料研究学报, 2005, 19(1): 1-7.

摘要 参考文献 相关文章 Metrics 全文: PDF(1623 KB)   摘要: 研究了加载频率、溶液pH值、氯离子浓度和氟化物转化膜等对挤压镁合金 AM60疲劳寿命的影响, 讨论了疲劳机理及AlMn相的作用. 结果表明: 在空气中10 Hz以下, 疲劳寿命与频率有一定的关系; 而在10 Hz以上, 疲劳寿命与频率无关. AM60在中性溶 液中疲劳寿命最短, 在碱性溶液中疲劳寿命最长. 氯离子能明显地降低疲劳寿命, 含氟转化膜提高腐蚀疲劳寿命的作用不明显. 断口分析表明, 挤压镁合金AM60疲劳裂纹的形成与AlMn 相粒子有关. 在空气中, 疲劳裂纹源为AlMn相粒子; 而在溶液介质中, 腐蚀疲劳裂纹萌生于AlMn相粒子周围的点蚀坑. 关键词 ： 材料失效与保护,  挤压镁合金,  腐蚀疲劳,  AlMn     Abstract：The effect of loading frequencies, pH values, chlorine ions and the fluorine--containing conversion film on fatigue life of as--extruded magnesium alloy AM60 was studied using a tensile--tension fatigue machine. The fractographic morphologies were observed by SEM, and the mechanisms of fatigue and the roles of AlMn particles were mainly discussed. The results showed that the fatigue life in ambient air has some relationship to the loading frequency when the frequency is lower than 10 Hz, and little relationship with ~loading ~frequency ~when ~greater ~than ~10 Hz. The fatigue life decreased in neutral solution, and increased in base solution with pH12. The conversion film containing fluorine can hardly improve the fatigue life. The fractography showed that fatigue crack initiations were related to AlMn particles. Fatigue cracks emanated at AlMn particles in air, while in aqueous solutions, it initiated the corrosion pits bordering upon the AlMn particles. Key words： materials failure and protection    as-extruded magnesium alloy    corrosion fatigue    fluorine-containing c 收稿日期: 2004-04-07      ZTFLH:  TG146   服务 把本文推荐给朋友 加入引用管理器 E-mail Alert RSS 作者相关文章 曾荣昌 韩恩厚 柯伟 刘路 徐永波 44.8K 链接本文: https://www.cjmr.org/CN/Y2005/V19/I1/1 1 S.L.Gouling, Met Eng. Quart, 12(2), 7(1970) 2 ZENG Rongchang, HAN Enhou, LIU Lu, XU Yongbo, KE Wei, Chinese Journal of Materials Research,17(3),241(2003)(曾荣昌,韩恩厚,刘路,徐水波,柯伟,材料研究学报,17(3),241(2003)) 3 ZENG Rongchang, The Study on Corrosion and Corrosion Fatigue of Wrought Magnesium Alloys, Ph.D Thesis, Institute of Metals Research, The Chinese Academy of Sciences, 2003(曾荣昌,变形镁合金的腐蚀与腐蚀疲劳行为研究,博士论文,中国科学院金属研究所,2003) 4 H.R.Mayer, H.Lipowsky, M.Papakyriacou, R.Rosch, A.Stich, S.Stanzl-Tschegg, Fatigue Fract Eng Mater Struct, 22, 591(1999) 5 M.F.Horstemeyer, N.Yang, K.Gall, D.Mcdowell, J.Fan, P.Gullett, Fatigue Fract Eng Mater Struct, 25, 1045(2002) 6 M.Papakyriacou, H.Mayer, U.Fuchs, S.E.Stanzl-Tschegg, R.P.Wei, Fatigue Fract Eng Mater Struct, 25, 795(2002) 7 U.Fuchs, H.J.Liowsky, H.Mayer, M.Papakyriacou, A.Stich, S-Tschegg, B.Zettl, Mat.-wiss.u.Werkstofftech., 33, 15(2002) 8 U.Fuchs, H.J.Liowsky, H.Mayer, M.Papakyriacou, A.Stich, S-Tschegg, B.Zettl, Mat.-wiss. u. Werk-stofftech., 33, 117(2002) 9 T.S.Shih, W.S.Liu, Y.J.Chen, Mater. Sci. Eng., A325, 152(2002) 10 A.Eliezer, E. M.Gutman, E.Abramov, Unigovski Ya, J. Light Metals, 1, 179(2001) 11 T.K.Aune, D.L.Albright, O.rjasaeter, O.K.Nerdahl, Elements of the Fatigue Process in Magnesium Die Casting Alloys, in Magnesium Technology , edited by H I Kaplan, J N Hryn, B B Clow (Warrendale, TMS. 2000) p.319 12 ZHU Zufang, Corrosion Resistance and Application of Non-Ferrous Metals (Beijing, Chemistry Industry Press, 1999)p.72(朱祖芳,有色金属的耐腐蚀性及其应用,北京,化学工业出版社,1999)p.72) 13 E.M.Gutman, Unigovski Ya, A.Eliezer, E.Abramov, L.Riber, Light Metal Age, 14(2000) 14 M.Hilpert, L.Wagner, J. Mater. Eng. Performance, 9, 402(2000) 15 T.Kanadani, A.Saijo, M.Hino K.Saki, J. Jpn. Inst. Light Metals, 52(10), 477(2002) 16 ZENG Rongchang, HAN Enhou, KE Wei, Acta Metall Sinica, 44(3), (2005)(曾荣昌,韩恩厚,柯伟,金属学报,44(3),(2005)) 17 ZHOU Xiangyang, KE Wei, Acta Metall Sinica, 3, 320(1990) [1] 高巍, 刘江南, 魏敬鹏, 要玉宏, 杨巍. TC4钛合金表面氧化亚铜掺杂微弧氧化层的结构和性能[J]. 材料研究学报, 2022, 36(6): 409-415. [2] 杨留洋, 谭卓伟, 李同跃, 张大磊, 邢少华, 鞠虹. 利用WBE及EIS测试技术对管道缺陷区动态冲刷腐蚀行为的研究[J]. 材料研究学报, 2022, 36(5): 381-391. [3] 陈铮, 杨芳, 王成, 杜瑶, 卢壹梁, 朱圣龙, 王福会. 惰性无机填料比例和颗粒尺寸对纳米Al/Al2O3 改性有机硅涂料抗高温氧化行为的影响[J]. 材料研究学报, 2022, 36(4): 271-277. [4] 李玉峰, 张念飞, 刘丽爽, 赵甜甜, 高文博, 高晓辉. 含磷石墨烯的制备及复合涂层的耐蚀性能[J]. 材料研究学报, 2022, 36(12): 933-944. [5] 陈艺文, 王成, 娄霞, 李定骏, 周科, 陈明辉, 王群昌, 朱圣龙, 王福会. 无机复合涂层对CB2铁素体耐热钢在650℃水蒸气中的防护[J]. 材料研究学报, 2021, 35(9): 675-681. [6] 唐荣茂, 刘光明, 刘永强, 师超, 张帮彦, 田继红, 甘鸿禹. 用电化学噪声技术研究Q235钢在含氯盐模拟混凝土孔隙液中的腐蚀行为[J]. 材料研究学报, 2021, 35(7): 526-534. [7] 张大磊, 魏恩泽, 荆赫, 杨留洋, 豆肖辉, 李同跃. 超级铁素体不锈钢表面超疏水结构的制备及其耐腐蚀性能[J]. 材料研究学报, 2021, 35(1): 7-16. [8] 王冠一, 车欣, 张浩宇, 陈立佳. Al-5.4Zn-2.6Mg-1.4Cu合金板材的低周疲劳行为[J]. 材料研究学报, 2020, 34(9): 697-704. [9] 黄安然, 张伟, 王学林, 尚成嘉, 范佳杰. 铁素体不锈钢在高温尿素环境中的腐蚀行为研究[J]. 材料研究学报, 2020, 34(9): 712-720. [10] 公维炜, 杨丙坤, 陈云, 郝文魁, 王晓芳, 陈浩. 扫描电化学显微镜原位观察碳钢涂层缺陷处的交流腐蚀行为[J]. 材料研究学报, 2020, 34(7): 545-553. [11] 郭铁明, 徐秀杰, 张延文, 宋志涛, 董志林, 金玉花. Q345q桥梁钢和Q345qNH耐候钢在模拟工业大气+除冰盐混合介质中的腐蚀行为[J]. 材料研究学报, 2020, 34(6): 434-442. [12] 朱金阳, 谭成通, 暴飞虎, 许立宁. 一种新型含Al低Cr合金钢在模拟油田采出液环境下的CO2腐蚀行为[J]. 材料研究学报, 2020, 34(6): 443-451. [13] 梁新磊, 刘茜, 王刚, 王震宇, 韩恩厚, 王帅, 易祖耀, 李娜. 氧化石墨烯改性环氧隔热涂层的耐蚀和隔热性能研究[J]. 材料研究学报, 2020, 34(5): 345-352. [14] 王志虎,张菊梅,白力静,张国君. 水热处理对AZ31镁合金微弧氧化陶瓷层组织结构及耐蚀性的影响[J]. 材料研究学报, 2020, 34(3): 183-190. [15] 段体岗, 黄国胜, 马力, 彭文山, 张伟, 许立坤, 林志峰, 何华, 毕铁满. Q235/Ni-Co基自修复涂层的制备和耐蚀性能[J]. 材料研究学报, 2020, 34(10): 777-783. Viewed Full text Abstract Cited   Shared      Discussed