波浪型倾斜板振动对Al--6Si--2Mg合金凝固组织的影响

材料研究学报

2008, Vol. 22

Issue (6): 639-644

研究论文

本期目录 | 过刊浏览

波浪型倾斜板振动对Al--6Si--2Mg合金凝固组织的影响

谢丰广^1†;管仁国²;王超²;刘相华¹

1.东北大学轧制技术及连轧自动化国家重点实验室沈阳 110004
2.东北大学材料与冶金学院沈阳 110004

Effects of parameters of vibrating wavelike sloping plate process on microstructures of Al–6Si–2Mg alloy

XIE Fengguang^1†; GUAN Renguo²; WANG Chao²; LIU Xianghua¹

1.State Key Lab. of Rolling & Automation; Northeastern University; Shenyang 110004
2.Materials & Metallurgical College; Northeastern University; Shenyang 110004

引用本文:

谢丰广管仁国王超刘相华. 波浪型倾斜板振动对Al--6Si--2Mg合金凝固组织的影响[J]. 材料研究学报, 2008, 22(6): 639-644.
, , , . Effects of parameters of vibrating wavelike sloping plate process on microstructures of Al–6Si–2Mg alloy[J]. Chin J Mater Res, 2008, 22(6): 639-644.

全文: PDF(1247 KB)

摘要:

研究了波浪型倾斜板振动参数对Al--6Si--2Mg合金凝固组织的影响, 结果表明:倾斜板的倾角和长度影响合金在斜板表面的流动剪切强度和剪切时间, 从而影响合金的组织.当浇注温度为660 --690℃时, 随着浇注温度的降低, 合金晶粒细化和球化,平均晶粒直径为40μm, 晶粒平均圆度值为2.5; 浇注温度低于660℃时,晶粒有粗化和枝晶化的趋势. 倾斜板的振动作用使表面形成的晶核离开表面进入熔体中,有效地减少了晶粒之间的粘连, 解决了结壳问题, 提高了形核率, 细化了组织;随着倾斜板振动频率的提高, 晶粒的平均圆度先降低后提高, 振动频率为50--60 Hz 出现最小值.倾斜板的波浪形表面对流动的金属具有搅拌作用, 增大了熔体内部的剪切作用,使晶粒更加细小圆整.

关键词 ：金属材料, 波浪型倾斜板, 振动, 半固态, 凝固组织

Abstract：

Effects of parameters of Vibrating Wavelike Sloping Plate process (VWSP) on solidification microstructures of Al–6Si–2Mg alloy were investigated. The results show that sloping angle and sloping plate length can affect the shear strength and shear time of the flow alloy on the sloping plate and thus influence alloy microstructure. When the casting temperature is in the range from 660℃ to 690 ℃, grain refining and spheroidization proceed with the decrease of casting temperature, the average grain size is 40 μm and the average grain roundness is 2.5. When the casting temperature is lower than 660℃, dendrite coarsening appears. The vibrating of the sloping plate can lead the nucleus forming on the sloping plate surface to escape off the sloping plate and disperse in the melt, which not only can effectively avoid grain connecting and solidification shell happening but also can improve the nucleation rate and refine microstructure. With the increase of vibration frequency, grain roundness decreases first and then increases, when the vibration frequency is in the range from 50 Hz to 60 Hz, the grain roundness reaches the minimum value. Wavelike sloping plate surface had a stirring function on the flowing alloy, which improved the shear strength in the alloy and caused grains became finer and more round.

Key words： Wavelike sloping plate;Vibrating;Semisolid;Solidification microstructure

收稿日期: 2008-06-03

ZTFLH:

TG111

基金资助:

国家自然科学基金(50604007);国家863计划新材料领域(2007AA03111)

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	谢丰广
	管仁国
	王超
	刘相华
44.8K

链接本文:

https://www.cjmr.org/CN/ 或 https://www.cjmr.org/CN/Y2008/V22/I6/639

1 M C Flemings, Behavior of metal alloys in the semisolid state, Metall. Trans, 22A, 957(1991)
2 MAO Weimin, ZHAO Aimin, ZHONG Xueyou, Spherical microstructure formation of the semisolid high chromium cast iron Cr20Mo2, Acta Metallurgica Sinica, 17(1),77(2004)
3 T Y Liu, H V Atkinson, P Kapranos, D H Kirkwood, Rapid compression of aluminum alloys and its relationship to thixoformability, Metallurgical and Materials Transactions, 34A(7), 1545(2003)
4 MAO Weimin, ZHEN Zisheng, CHEN Hongtao, Microstructure of semi–solid AZ91D alloysolidified during electromagnetic stirring, Chinese Journal of Materials Research, 19(3), 303(2005)
(毛卫民, 甄子胜, 陈洪涛, 电磁搅拌对半固态AZ91D镁合金组织的影响, 材料研究学报, 19(3), 303(2005))
5 Z Fan, Semisolid metal processing, International Materials Reviews, 47(2), 49(2002)
6 WU Shusen, WU Xueping, XIAO Zehui, A model of growth morphology for semisolid metals, Acta Materialia, 52(12), 3519(2004)
7 GUAN Renguo, WANG Shuncheng, WEN Jinglin, A continuous semisolid extending–extrusion process for producing AA2017 aluminum alloy flat bar, Mater. Sci. Tech., 22(6), 706(2006)
8 T Haga, Semisolid strip casting using a twin roll caster equipped with a cooling slope, J. of Mater. Proc. Tech., 130(20), 558(2002)
9 T Haga, T Kenta, I Masaaki, Twin roll casting aluminum alloy strips, J. of Mater. Proc. Tech., 153(10), 42(2004)
10 GUAN Renguo, WANG Chao, XING Zhenhuan, Novel sloping plate process for semisolid metal forming, Materials Science and Technology, 23(4), 438(2007)
11 GUAN Renguo, KANG Liwei, DU Haijun, SHANG Jianhong, WEN Jinglin, Preparing semisolid billet of Al– 3%Mg alloy by sloping shearing process, The Chinese Journal of Nonferrous Metals, 16(5), 812(2006)
(管仁国, 康立文, 杜海军, 尚剑洪, 温景林, 倾斜式冷却剪切技术制备Al-3%Mg半固态合金坯料,中国有色金属学报, 16(5), 812(2006))
12 LI Tao, HUANG Weidong, LIN Xin, Formation of globular structure during semisolid materal processing, The Chinese Journal of Nonferrous Metals, 10(5), 636(2000)
(李涛, 黄卫东, 林鑫, 半固态处理中球形晶形成与演化的直接观察, 中国有色金属学报, 10(5), 636(2000))
13 S.C.Wang, F.Cao, R.G.Guan, Formation and evolution of non–dendritic microstructures of semi–solid A2017 alloy prepared by SCR process. J. Mater. Sci. Tech., 22(2), 5(2006)

[1]	毛建军, 富童, 潘虎成, 滕常青, 张伟, 谢东升, 吴璐. AlNbMoZrB系难熔高熵合金的Kr离子辐照损伤行为[J]. 材料研究学报, 2023, 37(9): 641-648.
[2]	宋莉芳, 闫佳豪, 张佃康, 薛程, 夏慧芸, 牛艳辉. 碱金属掺杂MIL125的CO₂ 吸附性能[J]. 材料研究学报, 2023, 37(9): 649-654.
[3]	赵政翔, 廖露海, 徐芳泓, 张威, 李静媛. 超级奥氏体不锈钢24Cr-22Ni-7Mo-0.4N的热变形行为及其组织演变[J]. 材料研究学报, 2023, 37(9): 655-667.
[4]	邵鸿媚, 崔勇, 徐文迪, 张伟, 申晓毅, 翟玉春. 空心球形AlOOH的无模板水热制备和吸附性能[J]. 材料研究学报, 2023, 37(9): 675-684.
[5]	幸定琴, 涂坚, 罗森, 周志明. C含量对VCoNi中熵合金微观组织和性能的影响[J]. 材料研究学报, 2023, 37(9): 685-696.
[6]	欧阳康昕, 周达, 杨宇帆, 张磊. 含LPSO相Mg-Y-Er-Ni合金的组织和拉伸性能[J]. 材料研究学报, 2023, 37(9): 697-705.
[7]	徐利君, 郑策, 冯小辉, 黄秋燕, 李应举, 杨院生. 定向再结晶对热轧态Cu71Al18Mn11合金的组织和超弹性性能的影响[J]. 材料研究学报, 2023, 37(8): 571-580.
[8]	熊诗琪, 刘恩泽, 谭政, 宁礼奎, 佟健, 郑志, 李海英. 固溶处理对一种低偏析高温合金组织的影响[J]. 材料研究学报, 2023, 37(8): 603-613.
[9]	刘继浩, 迟宏宵, 武会宾, 马党参, 周健, 徐辉霞. 喷射成形M3高速钢热处理过程中组织的演变和硬度偏低问题[J]. 材料研究学报, 2023, 37(8): 625-632.
[10]	由宝栋, 朱明伟, 杨鹏举, 何杰. 合金相分离制备多孔金属材料的研究进展[J]. 材料研究学报, 2023, 37(8): 561-570.
[11]	任富彦, 欧阳二明. g-C₃N₄ 改性Bi₂O₃ 对盐酸四环素的光催化降解[J]. 材料研究学报, 2023, 37(8): 633-640.
[12]	王昊, 崔君军, 赵明久. 镍基高温合金GH3536带箔材的再结晶与晶粒长大行为[J]. 材料研究学报, 2023, 37(7): 535-542.
[13]	刘明珠, 樊娆, 张萧宇, 马泽元, 梁城洋, 曹颖, 耿仕通, 李玲. SnO₂ 作散射层的光阳极膜厚对量子点染料敏化太阳能电池光电性能的影响[J]. 材料研究学报, 2023, 37(7): 554-560.
[14]	秦鹤勇, 李振团, 赵光普, 张文云, 张晓敏. 固溶温度对GH4742合金力学性能及γ' 相的影响[J]. 材料研究学报, 2023, 37(7): 502-510.
[15]	刘天福, 张滨, 张均锋, 徐强, 宋竹满, 张广平. 缺口应力集中系数对TC4 ELI合金低周疲劳性能的影响[J]. 材料研究学报, 2023, 37(7): 511-522.

Viewed

Full text

Abstract

Cited

Shared

Discussed