材料研究学报  2004, Vol. 18 Issue (5): 517-523

论文 本期目录 | 过刊浏览 |

锂对低Cu/Mg比Al--Cu--Mg--Ag合金时效特性的影响

陈志国;郑子樵;王芝秀;李世晨

中南大学

Influence of Li on the ageing characteristics and microstructure of Al--Cu--Mg--Ag alloy with low Cu/Mg ratio

;;;

中南大学

陈志国; 郑子樵; 王芝秀; 李世晨 . 锂对低Cu/Mg比Al--Cu--Mg--Ag合金时效特性的影响[J]. 材料研究学报, 2004, 18(5): 517-523.
, , , . Influence of Li on the ageing characteristics and microstructure of Al--Cu--Mg--Ag alloy with low Cu/Mg ratio[J]. Chin J Mater Res, 2004, 18(5): 517-523.

摘要 参考文献 相关文章 Metrics 全文: PDF(2672 KB)   摘要: 通过时效硬化曲线的测量、室温拉伸实验以及时效组织的电镜观察, 研究了添加锂对低Cu/Mg比Al--Cu--Mg--Ag合金时效特性的影响. 结果表明, 在Al--4.0Mg--1.5Cu--0.4Ag合金中添加锂, 可以加速合金的时效进程, 但其时效硬化效果并不能简单地随着含锂量的增加而逐步加强, 只有当锂含量达到2.0\%(质量分数)时, 才表现出显著的时效硬化与强化效果. 含2.0\%Li的Al--4.0Mg--1.5Cu--0.4Ag合金中$Z$相、$\delta^{\prime}$以及 $\delta^{\prime}$/$\beta^{\prime}$复合粒子的弥散析出是产生显著时效硬化与强化的原因. 关键词 ： 金属材料,  铝合金,  时效,  微观结构,  锂     Abstract：The influence of lithium on the ageing behavior and microstructure of the low Cu/Mg ratio Al--Cu--Mg--Ag alloys was investigated. The results show that the effect of Li is to increase the rate of hardening, however, the addition of lithium does not progressively change age hardening and precipitation process of Al--Cu--Mg--Ag alloys with low Cu/Mg ratio, and significant age hardening response only occurs with the addition of 2.0\%Li (mass fraction). Transmission electron microscope (TEM) investigation results show that the remarkable increase of age hardness and strength is attributed to the fine dispersion of $\delta^{\prime}$, $Z$ phase and spherical $\delta^{\prime}$/$\beta^{\prime}$ compound particles in the 2.0\%Li--containing alloy. Key words： metallic materials    Al alloy    ageing    microstructure    lithium 收稿日期: 2004-11-05      ZTFLH:  TG113   服务 把本文推荐给朋友 加入引用管理器 E-mail Alert RSS 作者相关文章 陈志国 郑子樵 王芝秀 李世晨 44.8K 链接本文: https://www.cjmr.org/CN/      或      https://www.cjmr.org/CN/Y2004/V18/I5/517 1 I.J.Polmear, Materials Forum, 23, 117(1999) 2 S.P.Ringer, K.Raviprasad, Materials Forum, 24, 59(2000) 3 I.J.Polmear, Materials Science Forum, 13/14, 195(1987) 4 H.D.Chopra, L.J.Liu, B.C.Muddle, I.J. Polmear, Philosophical Magazine Letters, 71(6) , 319(1995) 5 S.P.Ringer, K.Hono, Materials Characterization, 44, 101(2000) 6 Y.C.Chang, J.M.Howe, Metallurgical Transaction, 24A, 1461(1993) 7 J.M. Howe, Philosophical Magazine Letters, 70(3) , 111(1994) 8 B.C.Muddle, I.J.Polmear, Acta Metall., 37(3) , 777(1989) 9 V.D.Scott, S.Ketty, R.L.Trumper, Materials Transactions JIM, 38(5) , 478(1997) 11 H.D.Chopra, L.J.Liu, B.C.Muddle, I.J.Polmear, Philosophical Magazine Letters, 73(6) , 351(1996) 12 E.J.Lavernia, T.S.Srivatsan, F.A.Mohamed, Journal of Materials Science, 25, 1137(1990) 13 I.J.Polmear, R.J.Chester, Scripta Metallurgica, 23, 1213(1989) 14 E.A.Starke, Jr., Journal of the Japan Institute of Light Metals, 51, 77(2001) 15 J.N.Pennington, Modern Metal, 55(2) , 10(2000) 16 P.S.Fielding, G.J.Wolf, Advanced Materials & Processes, 150(4) , 21(1996) 17 S.P.Ringer, G.C.Quan, T.Sakurai, Solute Clustering, Materials Science and Engineering A, 250, 120(1998) 18 C.H.Joh, T.Katsube, K.Yamada, Y.Miura, in: Proceedings of the 6th International Conference on Alu-minium alloys, Effect of Sc Addition on the Precipitation Behaviour of an Al-Li-Mg-Cu Alloy, edited by T. Sato, S.Kumai, T.Kobayashi and Y.Murakarni(Toyohashi, Japan: The Japan institute of Light Metals, 1998) p.799 19 J.F.Nie, B.C.Muddle, I.J.Polmear, Materials Science Forum, 217～222, 1257(1996) 20 E.A.Starke, Jr., F.S.Lin, Metallurgical Transactions A, 13, 2259(1982) 21 N.J.Kim, S.K.Das, Scripta Metall., 20(8) , 1107(1986) 22 K.K.Sankaran, J.E.O'neal, S.M.L.Sastry, Metallurgical Transactions A, 14, 2174(1983) 23 B.P.Huang, Z.Q.Zheng, Acta Mater., 46(12) , 4381(1998) 24 A.K.Niessen, F.R.de Boer, R..Boom, P.F.de Chatel, W.C.M.Mattens, A.R.Miedema, Calphad, 7(1) , 51(1983) [1] 毛建军, 富童, 潘虎成, 滕常青, 张伟, 谢东升, 吴璐. AlNbMoZrB系难熔高熵合金的Kr离子辐照损伤行为[J]. 材料研究学报, 2023, 37(9): 641-648. [2] 宋莉芳, 闫佳豪, 张佃康, 薛程, 夏慧芸, 牛艳辉. 碱金属掺杂MIL125的CO2 吸附性能[J]. 材料研究学报, 2023, 37(9): 649-654. [3] 赵政翔, 廖露海, 徐芳泓, 张威, 李静媛. 超级奥氏体不锈钢24Cr-22Ni-7Mo-0.4N的热变形行为及其组织演变[J]. 材料研究学报, 2023, 37(9): 655-667. [4] 邵鸿媚, 崔勇, 徐文迪, 张伟, 申晓毅, 翟玉春. 空心球形AlOOH的无模板水热制备和吸附性能[J]. 材料研究学报, 2023, 37(9): 675-684. [5] 幸定琴, 涂坚, 罗森, 周志明. C含量对VCoNi中熵合金微观组织和性能的影响[J]. 材料研究学报, 2023, 37(9): 685-696. [6] 欧阳康昕, 周达, 杨宇帆, 张磊. 含LPSO相Mg-Y-Er-Ni合金的组织和拉伸性能[J]. 材料研究学报, 2023, 37(9): 697-705. [7] 徐利君, 郑策, 冯小辉, 黄秋燕, 李应举, 杨院生. 定向再结晶对热轧态Cu71Al18Mn11合金的组织和超弹性性能的影响[J]. 材料研究学报, 2023, 37(8): 571-580. [8] 熊诗琪, 刘恩泽, 谭政, 宁礼奎, 佟健, 郑志, 李海英. 固溶处理对一种低偏析高温合金组织的影响[J]. 材料研究学报, 2023, 37(8): 603-613. [9] 刘继浩, 迟宏宵, 武会宾, 马党参, 周健, 徐辉霞. 喷射成形M3高速钢热处理过程中组织的演变和硬度偏低问题[J]. 材料研究学报, 2023, 37(8): 625-632. [10] 由宝栋, 朱明伟, 杨鹏举, 何杰. 合金相分离制备多孔金属材料的研究进展[J]. 材料研究学报, 2023, 37(8): 561-570. [11] 任富彦, 欧阳二明. g-C3N4 改性Bi2O3 对盐酸四环素的光催化降解[J]. 材料研究学报, 2023, 37(8): 633-640. [12] 王昊, 崔君军, 赵明久. 镍基高温合金GH3536带箔材的再结晶与晶粒长大行为[J]. 材料研究学报, 2023, 37(7): 535-542. [13] 刘明珠, 樊娆, 张萧宇, 马泽元, 梁城洋, 曹颖, 耿仕通, 李玲. SnO2 作散射层的光阳极膜厚对量子点染料敏化太阳能电池光电性能的影响[J]. 材料研究学报, 2023, 37(7): 554-560. [14] 季雨辰, 刘树和, 张天宇, 查成. MXene在锂硫电池中应用的研究进展[J]. 材料研究学报, 2023, 37(7): 481-494. [15] 秦鹤勇, 李振团, 赵光普, 张文云, 张晓敏. 固溶温度对GH4742合金力学性能及γ' 相的影响[J]. 材料研究学报, 2023, 37(7): 502-510. Viewed Full text Abstract Cited   Shared      Discussed