磁场方向对碱腐蚀构建多晶硅绒面结构的影响
宋建宇, 李想, 王启安, 沈龙海, 齐东丽, 冯瑜(), 陈建金
沈阳理工大学理学院 沈阳 110159
Effect of Magnetic Field Direction on Suede Structure of Alkaline Solution Corroded Polysilicon
SONG Jianyu, LI Xiang, WANG Qian, SHEN Longhai, QI Dongli, FENG Yu(), CHEN Jianjin
School of Science, Shenyang Ligong University, Shenyang 110159, China
引用本文:

宋建宇, 李想, 王启安, 沈龙海, 齐东丽, 冯瑜, 陈建金. 磁场方向对碱腐蚀构建多晶硅绒面结构的影响[J]. 材料研究学报, 2021, 35(9): 682-688.
Jianyu SONG, Xiang LI, Qian WANG, Longhai SHEN, Dongli QI, Yu FENG, Jianjin CHEN. Effect of Magnetic Field Direction on Suede Structure of Alkaline Solution Corroded Polysilicon[J]. Chinese Journal of Materials Research, 2021, 35(9): 682-688.

全文: PDF(3798 KB)   HTML
摘要: 

在零磁场和2T、4T磁场中用NaOH溶液腐蚀制备多晶硅绒面结构,样品板平面分别平行和垂直于磁场放置。用电子天平称重表征硅片的腐蚀程度、用奥林巴斯LEXT OLS4100共聚焦显微镜观察多晶硅片形貌、用Ocean Optics USB4000光谱仪测量多晶硅片的反射率、用WT-1200硅片测试仪测量样品的少子寿命,研究了磁场方向对碱腐蚀构建多晶硅绒面结构的影响。结果表明:随着磁感应强度的提高多晶硅片的腐蚀程度严重,绒面结构变得均匀和细腻,反射率降低;在磁感应强度相同的条件下碱液中沿着磁场方向运动的OH-离子不受磁场力作用,而运动方向与磁场方向不完全一致的OH-离子受磁场产生的Lorenz力作用。Lorenz力使板平面垂直于磁场方向的硅片样品腐蚀程度更加严重、绒面和断层状结构细腻程度更加显著、少子的寿命更长、反射率更低。磁感应强度为4T时反射率降低到14.5%,在用碱液腐蚀制备多晶硅绒面结构过程中施加强磁场,板平面垂直磁场方向放置硅片减反射效果更加显著。

关键词 无机非金属材料磁场方向碱液腐蚀多晶硅Lorenz力绒面结构    
Abstract

The surface suede texture of polysilicon wafer was prepared via NaOH solution etching process. The effect of direction (to which the wafer parallel or perpendicular) and intensity (0, 2 or 4T) of the applied magnetic field on the surface texture of polysilicon wafer was investigated by means of weight loss measurement, Olympus LEXT OLS4100 confocal microscope, ocean Optics USB4000 spectrometer and WT-1200 silicon wafer tester. The results show that with the increase of magnetics intensity the corrosion degree of polysilicon wafer increases, and that the suede texture becomes uniform and finer, whereas the reflectivity decreases. With the same applied magnetics intensity, the motion direction of OH- ions along the magnetic field direction in the alkali solution were not affected by the magnetic field force, however, the Lorenz force generated by the magnetic field acts on OH- ions, when who's motion direction is not exactly in line with the direction of the magnetic field, which then resulted in stronger corrosion for the silicon wafer placed perpendicular to the magnetic field direction, in consequence, the wafer presents much finer in suede texture and stratified structure with longer subatomic lifetime and lower reflectivity, peculiarly the applied magnetics intensity of 4T could make the reflectivity of the wafer lower to 14.5%. In fact, the surface reflectivity of the polysilicon wafer can be significantly reduced when the polysilicon wafer placed perpendicular to the direction of applied magnetic field during the preparation of surface suede texture with the NaOH solution etching process.

Key wordsinorganic non-metallic materials    magnetic field direction    alkali corrosion    polysilicon    lorentz force    suede structure
收稿日期: 2020-12-17     
ZTFLH:  TM914.4  
基金资助:辽宁省自然基金指导计划(2019-ZD-0254)
作者简介: 宋建宇,男,1969年生,副教授
图1  在零磁场条件下处理的多晶硅片其形貌和表面三维高度
图2  在2T磁场中处理的多晶硅片其形貌和表面三维高度
图3  在4T磁场中处理的多晶硅片其形貌和表面三维高度
图4  在不同强度磁场中处理多晶硅片的腐蚀程度
图5  在不同磁场中处理多晶硅片的光反射率
图6  在不同磁场中处理多晶硅片的少数载流子寿命
1 Zhou Z Z, Wu Z, Feng K P. A review on surface texturing technology for multicrysstalline silion [J]. Materials Reports, 2015,29(5): 55
1 周兆忠, 吴喆, 冯凯萍. 多晶硅表面制绒技术研究现状 [J]. 材料导报, 2015, 29(5): 55
2 Zechner C, Hahn G, Jooss W, et al. Systematic study towards high efficiency multicrystalline silicon solar cells with mechanical surface texturization[C]//Conference Record of the 1997 IEEE 26th Photovoltaic Specialists Conference. Anaheim, 1997: 243
3 Liu Z, Niu Y C, Jiang Y S, et al. Study on electrochemical etching of diamond wire sawn polycrystalline silicon wafer by double-bath method in KOH solution [J]. Contemporary Chemical Industry, 2019, 12: 2808
3 刘政, 牛玉超, 姜言森等. 双槽法KOH溶液电化学刻蚀金刚线切割多晶硅片的研究 [J]. 当代化工, 2019, 12: 2808
4 Dobrzanski L A, Drygala A, Panek P, et al. Development of the laser method of multicrystalline silicon surface texturization [J]. Archives of Materials Science and Engineering, 2009, 38(1): 5
5 Dobrzanski L A, Drygala A. Laser texturization in technology of multicrystalline silicon solar cells[J]. Journal of Achievements in Materials and Manufacturing Engineering, 2008, 29(1): 7
6 Wang X M, Zhao R Q, Shen H, et al. Laser surface texturation of multicrystalline silicon for solar cell [J]. Laser and Optoelectronics Progress, 2010, 47(1): 1
6 王学孟, 赵汝强, 沈辉等. 用于太阳能电池的多晶硅激光表面织构化研究 [J]. 激光与光电子学进展, 2010, 47(1): 1
7 Jia Z F,Song J Y, Zhao W Y. Influence of NaOH solution concentration to the surface texture of multicrystalline silicon by Laser ablation[J]. Journal of Jinggangshan University(Natural Science), 2019, 40(2): 83
7 贾子凡, 宋建宇, 肇伟懿. NaOH溶液浓度对激光刻蚀多晶硅片表面织构的影响 [J]. 井冈山大学学报(自然科学版), 2019, 40(2): 83
8 Yoo J, Yu G, Yi J. Large-area multicrystalline silicon solar cell fabrication using reactive ion etching (RIE) [J]. Solar Energy Materials and Solar Cells, 2011, 95(1): 2
9 Qian Y, Feng S M. Study on micro-structure of polycrystalline silicon surface etched uing NaNO3 [J]. Semiconductor Optoelectronics, 2012, 33(1): 87
9 钱勇, 冯仕猛. 亚硝酸钠刻蚀液对多晶硅表面陷阱坑形貌的影响. 半导体光电, 2012, 33(1): 87
10 Bauer J, Wagner J M, Lotnyk A, et al. Hot spots in multicrystalline silicon solar cells: avalanche breakdown due to etch pits [J]. Physica Status Solidi (RRL)-Rapid Research Letters, 2009, 3(2-3): 40
11 Li Z C, Zhao L, Diao H W, et al. Study on antireflection effect of electrochemical corrosion of polysilicon substrate [J]. Solar Energy, 2013(2): 54
11 李兆辰, 赵雷, 刁宏伟等. 电化学腐蚀多晶硅衬底减反射效果研究 [J]. 太阳能, 2013(2): 54
12 Wu X W, Li J Y, Tan Y. Technology of preparing diamond wire cut multicrystallinesilicon wafer texture surface [J]. Journal of Inorganic Materials, 2017, 32(9):985
12 武晓玮, 李佳艳, 谭毅. 金刚石线锯切割多晶硅片表面制绒工艺研究 [J]. 无机材料学报, 2017, 32(9): 985
13 Gangopadhyay U, Dhungel S K, Kim K, et al. Novel low cost chemical texturing for very large area industrial multi-crystalline silicon solar cells [J]. Semiconductor Science and Technology, 2005, 20(9): 938
14 Wang K X, Feng S M, Xu H T, et al. Experimental study on microstructure of polycrystalline silicon with alkali etching [J]. Scientia Sinica(Technologica), 2012, 42(6): 643
14 王坤霞, 冯仕猛, 徐华天等. 碱液刻蚀的多晶硅不同晶面微结构实验研究 [J]. 中国科学: 技术科学, 2012, 42(6): 643
15 Chang X Y. Surface treatment of polycrystalline silicon and study on heterojunction solar cell [D]. Tianjin: Hebei University of Technology, 2017
15 常雪岩. 多晶硅表面处理及异质结太阳能电池的研究 [D]. 天津: 河北工业大学, 2017
16 Abburi M, Bostrm T, Olefjord I. Electrochemical isotropic texturing of mc-Si wafers in KOH solution [J]. Materials Chemistry and Physics, 2013, 139(2-3): 756
17 Kuang G L, Pi L. Scientific issues under high magnetic field. Chin Sci Bull [J]. Chinese Science Bulletin, 2016, 61(17): 1940
17 匡光力, 皮雳. 强磁场下的科学问题 [J]. 科学通报, 2016, 61(17): 1940
18 Cai S W, Ning F, Tang Y J, et al. Effect of magnetic field on anodic dissolution of iron in sodium perchlorate solution at different potentials [J]. Corrosion and Protection, 2020, 41(8): 1
18 蔡爽巍, 宁飞, 唐元杰等. 磁场对铁在不同电位高氯酸钠溶液中阳极溶解的影响 [J]. 腐蚀与防护, 2020, 41(8): 1
19 Zhao J, Wang T P, Zhang H H. Effect of SDBS Coupled with Magnetic Field on Corrosion Inhibition Performance and Specific Capacitance of Anodic Aluminum Foil. Materials Reports, 2020, 34(06): 6156
19 赵静, 王天鹏, 张淮浩. 磁场作用下十二烷基苯磺酸钠对阳极铝箔的缓蚀性能及比电容的影响 [J]. 材料导报, 2020, 34(06): 6156
20 Song J Y, Zhao W Y, Qi D L, et al. Effect of high magnetic field on surface texture of alkaline solution corroded polysilicon [J]. Surface Technology, 2020, 49(7): 120
20 宋建宇, 肇伟懿, 齐东丽等. 强磁场对碱液腐蚀制备多晶硅表面织构的影响 [J]. 表面技术, 2020, 49(7): 120
[1] 宋莉芳, 闫佳豪, 张佃康, 薛程, 夏慧芸, 牛艳辉. 碱金属掺杂MIL125CO2 吸附性能[J]. 材料研究学报, 2023, 37(9): 649-654.
[2] 邵鸿媚, 崔勇, 徐文迪, 张伟, 申晓毅, 翟玉春. 空心球形AlOOH的无模板水热制备和吸附性能[J]. 材料研究学报, 2023, 37(9): 675-684.
[3] 任富彦, 欧阳二明. g-C3N4 改性Bi2O3 对盐酸四环素的光催化降解[J]. 材料研究学报, 2023, 37(8): 633-640.
[4] 刘明珠, 樊娆, 张萧宇, 马泽元, 梁城洋, 曹颖, 耿仕通, 李玲. SnO2 作散射层的光阳极膜厚对量子点染料敏化太阳能电池光电性能的影响[J]. 材料研究学报, 2023, 37(7): 554-560.
[5] 李延伟, 罗康, 姚金环. Ni(OH)2 负极材料的十二烷基硫酸钠辅助制备及其储锂性能[J]. 材料研究学报, 2023, 37(6): 453-462.
[6] 余谟鑫, 张书海, 朱博文, 张晨, 王晓婷, 鲍佳敏, 邬翔. N掺杂生物炭的制备及其对Co2+ 的吸附性能[J]. 材料研究学报, 2023, 37(4): 291-300.
[7] 朱明星, 戴中华. SrSc0.5Nb0.5O3 改性BNT基无铅陶瓷的储能特性研究[J]. 材料研究学报, 2023, 37(3): 228-234.
[8] 刘志华, 岳远超, 丘一帆, 卜湘, 阳涛. g-C3N4/Ag/BiOBr复合材料的制备及其光催化还原硝酸盐氮[J]. 材料研究学报, 2023, 37(10): 781-790.
[9] 周毅, 涂强, 米忠华. 制备方法对磷酸盐微晶玻璃结构和性能的影响[J]. 材料研究学报, 2023, 37(10): 739-746.
[10] 谢锋, 郭建峰, 王海涛, 常娜. ZnO/CdS/Ag复合光催化剂的制备及其催化和抗菌性能[J]. 材料研究学报, 2023, 37(1): 10-20.
[11] 余超, 邢广超, 吴郑敏, 董博, 丁军, 邸敬慧, 祝洪喜, 邓承继. 亚微米Al2O3 对重结晶碳化硅的作用机制[J]. 材料研究学报, 2022, 36(9): 679-686.
[12] 方向明, 任帅, 容萍, 刘烁, 高世勇. 自供能Ag/SnSe纳米管红外探测器的制备和性能研究[J]. 材料研究学报, 2022, 36(8): 591-596.
[13] 李福禄, 韩春淼, 高嘉望, 蒋健, 许卉, 李冰. 氧化石墨烯的变温发光[J]. 材料研究学报, 2022, 36(8): 597-601.
[14] 朱晓东, 夏杨雯, 喻强, 杨代雄, 何莉莉, 冯威. Cu掺杂金红石型TiO2 的制备及其光催化性能[J]. 材料研究学报, 2022, 36(8): 635-640.
[15] 熊庭辉, 蔡文汉, 苗雨, 陈晨龙. ZnO纳米棒阵列和薄膜的同步外延生长及其光电化学性能[J]. 材料研究学报, 2022, 36(7): 481-488.