Chin J Mater Res  1992, Vol. 6 Issue (6): 503-506    DOI:

Current Issue | Archive | Adv Search |

INFLUENCE OF SOLUTE ATOMS IN DILUTE ALUMINIUM ON THE EARLY STAGE OF FATIGUE

FEI Guangtao;ZHU Zhengang(Laboratory of Internal Friction and Defects in Solids;Institute of Solid State Physics;Academia Sinica)

FEI Guangtao;ZHU Zhengang(Laboratory of Internal Friction and Defects in Solids;Institute of Solid State Physics;Academia Sinica). INFLUENCE OF SOLUTE ATOMS IN DILUTE ALUMINIUM ON THE EARLY STAGE OF FATIGUE. Chin J Mater Res, 1992, 6(6): 503-506.

Abstract References Related Articles Recommended Metrics Download:  PDF(319KB)  Export:  BibTeX | EndNote (RIS)       Abstract  Variations of the stress σ,internal friction Q~(-1)and ultrasonic attenuation Δαwith cycling number N under push-pull fatigue strain for Al-0.025wt-%Mg and 99.6wt-%Alpolycrystalline specimens were measured.Experimenial results indicate that the existance Key words:  fatigue      solute atom      stress      internal friction      ultrasonic attenuation      Received:  25 December 1992      Service E-mail this article Add to citation manager E-mail Alert RSS （） Articles by authors URL:  https://www.cjmr.org/EN/     OR     https://www.cjmr.org/EN/Y1992/V6/I6/503 1 Vorren O,Ryum N.Acta Metall,1987;35:855 2 Xia Y B(夏月波),Wang Z G(王中光),Wang R H(王仁卉).Phys Stat Sol(a),1990;120:125 3 Mughrabi H.Mater Sci Eng,1978;33:207 4 Wang Z G(王中光),K(?)T S(葛庭燧).Mater Sci Eng,1981;50:65 5 Ramaswami B,Russell W J.Mater Sci Eng,1979;39:117 6 陈贤芬,林栋梁.金属学报,1984;20:A169 7 费广涛,朱震刚.材料科学进展,1992;6(6) :498 8 朱震刚,周星,费广涛.仪器仪表学报,1988;9:396 [1] LIU Tianfu, ZHANG Bin, ZHANG Junfeng, XU Qiang, SONG Zhuman, ZHANG Guangping. Effect of Notch Stress Concentration Factors on Low-cycle Fatigue Performance of TC4 ELI Alloy[J]. 材料研究学报, 2023, 37(7): 511-522. [2] ZHOU Zhangrui, LV Peisen, ZHAO Guoqi, ZHANG Jian, ZHAO Yunsong, LIU Lirong. Stress Rupture Deformation Mechanism of Two "Replacement of Re by W" Type Low-cost Second-generation Nickel Based Single Crystal Superalloys at Elevated Temperatures[J]. 材料研究学报, 2023, 37(5): 371-380. [3] QIAN Chunhua, CUI Haitao, WEN Weidong. Investigation on Thermo-mechanical Fatigue Behavior of GH4169 Alloy[J]. 材料研究学报, 2023, 37(2): 145-151. [4] CHEN Ruizhi, LIU Lirong, GUO Shengdong, ZHANG Mai, LU Guangxian, LI Yuan, ZHAO Yunsong, ZHANG Jian. Microstructural Stability and Stress Rupture Property of a 6Re/3Ru Containing Nickel-based Single Crystal Superalloy[J]. 材料研究学报, 2023, 37(10): 721-730. [5] DENG Hailong, LIU Bing, GUO Yang, KANG Heming, LI Mingkai, LI Yongping. Prediction and Evaluation of Very-high Cycle Fatigue Strength of Carburized Cr-Ni Gear Steel Based on Interior Failure Mechanism[J]. 材料研究学报, 2023, 37(1): 55-64. [6] HE Yufeng, WANG Li, WANG Dong, WANG Shaogang, LU Yuzhang, GU Ashan, SHEN Jian, ZHANG Jian. Effect of Hot Isostatic Pressing on Microstructure of a Third-Generation Single Crystal Superalloy DD33[J]. 材料研究学报, 2022, 36(9): 649-659. [7] YANG Liuyang, TAN Zhuowei, LI Tongyue, ZHANG Dalei, XING Shaohua, JU Hong. Dynamic Corrosion Behavior of Pipeline Defects Characterized by WBE and EIS Testing Techniques[J]. 材料研究学报, 2022, 36(5): 381-391. [8] ZHANG Botao, LI Shuhui, LI Yongfeng, HAN Guofeng. Effect of Stress Triaxiality on Hydrogen Embrittlement Susceptibility of Quenched Boron Steel B1500HS[J]. 材料研究学报, 2022, 36(10): 739-746. [9] YANG Bing, LIU Chunzhong, GAO Enzhi, SUN Wei, LIU Ting, ZHANG Hongning, ZHU Mingwei, LU Tianni. Deformation Behavior of Cast and Annealed 2024 Al-alloy at Different Temperatures[J]. 材料研究学报, 2022, 36(10): 730-738. [10] ZHANG Guangcheng, YUAN Tianxiang, MA Delin, ZHOU Ping, GUO Chaoqun, ZHOU Yun, ZUO Xiaoqing. Comparision of Structure and Performance for Foamed Stainless Steels 410L and 430L[J]. 材料研究学报, 2021, 35(8): 597-605. [11] HUANG Yaqi, WANG Dong, LU Yuzhang, XIONG Ying, SHEN Jian. Fatigue Crack Initiation Behavior at Intermediate Temperature under High Stress Amplitude for Single Crystal Superalloy DD413[J]. 材料研究学报, 2021, 35(7): 510-516. [12] CUI Lu, KANG Wenquan, ZOU Fang, WEI Wenlan, LI Zhen, WANG Peng. High Temperature Low Cycle Fatigue Characteristics of Steam Turbine Rotor Steel 10%Cr[J]. 材料研究学报, 2021, 35(5): 371-380. [13] REN Yanjing, ZHANG Xinmeng, XUE Peng, NI Dingrui, XIAO Bolv, MA Zongyi. Fatigue Property of Friction Stir Welded 6005A Al Alloy Profiles[J]. 材料研究学报, 2021, 35(4): 271-276. [14] SHU Delong, YAN Zhi, WANG Daohong, XIE Jun, HOU Guichen, Naicheng SHENG, LI Jinguo, YU Jinjiang, SUN Xiaofeng, ZHOU Yizhou. Influence of C- and B-content on Solidification and High Temperature Stress Rupture Behavior of Nickel-based Superalloy K417G[J]. 材料研究学报, 2021, 35(4): 241-250. [15] CHEN Lifei, LUO Yunrong, ZHANG Yingqian, LI Hui, LI Xiulan, LIAO Wenli. Effect of Pre-corrosion by Salt Spray on Extremely Low Cycle Fatigue Performance of HRB400E Seismic Steel Bar[J]. 材料研究学报, 2021, 35(2): 101-109. No Suggested Reading articles found! Viewed Full text Abstract Cited   Shared      Discussed