材料研究学报  2004, Vol. 18 Issue (5): 499-505

论文 本期目录 | 过刊浏览 |

Bi--Mn合金中MnBi析出相磁致织构的形成

王晖;任忠鸣;王秋良;严陆光

中国科学院电工研究所

Textured structures of MnBi precipitated phase in Bi--Mn alloys solidified in a magnetic field

;;;

中国科学院电工研究所

王晖; 任忠鸣; 王秋良; 严陆光 . Bi--Mn合金中MnBi析出相磁致织构的形成[J]. 材料研究学报, 2004, 18(5): 499-505.
, , , . Textured structures of MnBi precipitated phase in Bi--Mn alloys solidified in a magnetic field[J]. Chin J Mater Res, 2004, 18(5): 499-505.

摘要 参考文献 相关文章 Metrics 全文: PDF(2550 KB)   摘要: 研究了Bi--6\%Mn合金从低于446℃开始的半固态凝固过程中, MnBi析出相磁致织构的形成过程和规律. 结果表明, 合金从355$\sim$446℃开始半固态凝固时, 合金中的MnBi相在340℃(MnBi相顺磁--铁磁转变温度)附近发生形态突变, 由规则的六方晶体转变为沿ab面长大的不规则片状晶体; 析出相的磁致织构是在发生磁性转变生成铁磁性MnBi相后通过晶粒旋转取向形成的. 合金从低于355℃开始半固态凝固, 导致织构形成的磁感应强度阈值随着温度的升高而降低, 从355$\sim$446℃之间开始的半固态凝固则相反. 磁场中合金从低于355℃开始的半固态凝固有利于制取高性能的过共晶Bi/MnBi磁性复合材料. 关键词 ： 金属材料,  凝固,  织构,  磁场,  Bi-Mn合金,  MnBi析     Abstract：Magnetic textured structures of MnBi precipitated phase in Bi--6\% Mn alloy were studied experimentally during solidification of the alloy from the semi solid zone below 446℃. An abrupt shape change of MnBi phase from regular hexagonal grains to oblate grains grown up along their ab--plane was observed firstly near 340℃, which is the transformation temperature of MnBi compound from paramagnetic state to ferromagnetic state. After the production of ferromagnetic MnBi grains from the magnetic transformation, the textured structures form by the rotation of the precipitated grains. The critical magnetic flux intensity for the textured structures decreases with increasing the heating temperature during solidification from the semi solid zone below 355℃ and increases between 355℃ and 446℃. Solidification from the semi solid zone below 355℃ is propitious to fabricate hypereutectic Bi/MnBi magnetic composites with excellent properties. Key words： metallic materials    solidification    textured structure    magnetic field    Bi-Mn alloy    MnBi precipitated ph 收稿日期: 2004-11-05      ZTFLH:  TG111   服务 把本文推荐给朋友 加入引用管理器 E-mail Alert RSS 作者相关文章 王晖 任忠鸣 王秋良 严陆光 44.8K 链接本文: https://www.cjmr.org/CN/      或      https://www.cjmr.org/CN/Y2004/V18/I5/499 1 T.M.Mulcahy, J.R.Hull, IEEE. Trans. Appl. Supercond., 13(2) , 1668(2003) 2 D.E.Farrel, B.S.Chandrasekhar, M.R.DeGuire, M.M.Fang, V.G.Kogan, J.R.Clem, D.K.Finnemore, Physical Review B, 36(7) , 4025(1987) 3 P.D.Rango, M.Lee, P.Lejay, A.Sulpice, R.Tournier, M.Ingold, P.Germi, M.Pernet, Nature, 349, 770(1991) 4 Y.Sakka, T.S.Suzuki, N.Tanabe, S.Asai, K.Kitazawa, Jap. J. Appl. Phys., 41(12) , L1416(2002) 5 A.Katsuki, R.Tokunaga, S. I.Watanabe, Chem. Lett., (8) , 607(1996) 6 WANG Hui, Effects of a High Magnetic Field on the Behavior of Precipitated Phases in Alloys, Ph.D Thesis, Shanghai University(2003) (王晖,强磁场对合金中析出相凝固行为的影响,博士论文,上海大学(2003) ) 7 H.Yasuda, I.Ohnaka, Y.Yamamoto, A. S.Wismogroho, N.Takezawa, K.Kishio, Mater. Trans., 44(12) , 2550(2003) 8 A.D.Sheikh-Ali, D. A.Molodov, H.Garmestani, Materials Science Forum, 408～412, 955(2003) 9 S.Asai, Modelling Simul. Mater. Sci. Eng., 12, R1(2004) 10 P.J.Ferreira, H.B.Liu, J.B.V.Sande, J. Mater. Res, 14(7) , 2751(1999) 11 T.Sugiyama, M.Tahashi, K.Sassa, S.Asai, ISIJ International, 43(6) , 855(2003) 12 J.L.Decarlo, R.G.Pirich, Metall. Trans. A, 15, 2155(1984) 13 M.N.Shetty, D.K.Rawat, K.N.Rai, J. Mater. Sci., 22, 1908(1987) 14 W.G.Moffatt, The Handbook of Binary Phase Diagrams (New York, General Electric Compony, 1984) 15 R.G.Pirich, G.Busch, W.Poit, D.J.Larson Jr, Metall. Trans. A, 11, 193(1980) 16 E.M.Savitsky, R.S.Torchinova, S.A.Turanov, J. Cryst. Growth., 52, 519(1981) 17 H.Yasuda, I.Ohnaka, Y.Yamamoto, K.Tokieda, K.Kishio, Mater. Trans., 44(10) , 2207(2003) 18 WANG Hui, REN Zhongming, DENG Kang, XU Kuangdi, Acta Metal. Sinica, 38(1) , 41(2002) (王晖,任忠鸣,邓康,徐匡迪,金属学报,38(1) ,41(2002) ) 19 H.Wang, Z.M.Ren, X.Li, W.X.Li, K.Deng, K.D.Xu, Transactions of Nonferrous Metals Society of China, 13(6) , 1405(2003) 20 T.Chen, J. Appl. Phys., 45(5) , 2358(1974) [1] 毛建军, 富童, 潘虎成, 滕常青, 张伟, 谢东升, 吴璐. AlNbMoZrB系难熔高熵合金的Kr离子辐照损伤行为[J]. 材料研究学报, 2023, 37(9): 641-648. [2] 宋莉芳, 闫佳豪, 张佃康, 薛程, 夏慧芸, 牛艳辉. 碱金属掺杂MIL125的CO2 吸附性能[J]. 材料研究学报, 2023, 37(9): 649-654. [3] 赵政翔, 廖露海, 徐芳泓, 张威, 李静媛. 超级奥氏体不锈钢24Cr-22Ni-7Mo-0.4N的热变形行为及其组织演变[J]. 材料研究学报, 2023, 37(9): 655-667. [4] 邵鸿媚, 崔勇, 徐文迪, 张伟, 申晓毅, 翟玉春. 空心球形AlOOH的无模板水热制备和吸附性能[J]. 材料研究学报, 2023, 37(9): 675-684. [5] 幸定琴, 涂坚, 罗森, 周志明. C含量对VCoNi中熵合金微观组织和性能的影响[J]. 材料研究学报, 2023, 37(9): 685-696. [6] 欧阳康昕, 周达, 杨宇帆, 张磊. 含LPSO相Mg-Y-Er-Ni合金的组织和拉伸性能[J]. 材料研究学报, 2023, 37(9): 697-705. [7] 徐利君, 郑策, 冯小辉, 黄秋燕, 李应举, 杨院生. 定向再结晶对热轧态Cu71Al18Mn11合金的组织和超弹性性能的影响[J]. 材料研究学报, 2023, 37(8): 571-580. [8] 熊诗琪, 刘恩泽, 谭政, 宁礼奎, 佟健, 郑志, 李海英. 固溶处理对一种低偏析高温合金组织的影响[J]. 材料研究学报, 2023, 37(8): 603-613. [9] 刘继浩, 迟宏宵, 武会宾, 马党参, 周健, 徐辉霞. 喷射成形M3高速钢热处理过程中组织的演变和硬度偏低问题[J]. 材料研究学报, 2023, 37(8): 625-632. [10] 由宝栋, 朱明伟, 杨鹏举, 何杰. 合金相分离制备多孔金属材料的研究进展[J]. 材料研究学报, 2023, 37(8): 561-570. [11] 任富彦, 欧阳二明. g-C3N4 改性Bi2O3 对盐酸四环素的光催化降解[J]. 材料研究学报, 2023, 37(8): 633-640. [12] 王昊, 崔君军, 赵明久. 镍基高温合金GH3536带箔材的再结晶与晶粒长大行为[J]. 材料研究学报, 2023, 37(7): 535-542. [13] 刘明珠, 樊娆, 张萧宇, 马泽元, 梁城洋, 曹颖, 耿仕通, 李玲. SnO2 作散射层的光阳极膜厚对量子点染料敏化太阳能电池光电性能的影响[J]. 材料研究学报, 2023, 37(7): 554-560. [14] 秦鹤勇, 李振团, 赵光普, 张文云, 张晓敏. 固溶温度对GH4742合金力学性能及γ' 相的影响[J]. 材料研究学报, 2023, 37(7): 502-510. [15] 刘天福, 张滨, 张均锋, 徐强, 宋竹满, 张广平. 缺口应力集中系数对TC4 ELI合金低周疲劳性能的影响[J]. 材料研究学报, 2023, 37(7): 511-522. Viewed Full text Abstract Cited   Shared      Discussed