单分散纳米介孔二氧化硅的制备

梁艳;张劲松;张军旗

中国科学院金属研究所

Preparation of monodisperse nanosized mesoporous silica

;;

中国科学院金属研究所

引用本文:

梁艳; 张劲松; 张军旗 . 单分散纳米介孔二氧化硅的制备[J]. 材料研究学报, 2004, 18(2): 149-154.

全文: PDF(2340 KB)

摘要: 在温和碱性条件下, 以十六烷基三甲基溴化铵为模板剂, 正硅酸乙酯为硅源, 三嵌段共聚物F127为助剂, 制备出粒径为60-80 nm的单分散纳米介孔二氧化硅MCM--41.研究了F127的用量对介孔结构和纳米粒子分散性的影响. 结果表明,适量的非离子表面活性剂F127具有助模板剂的作用,可以有效地提高纳米介孔粉体的有序性; 过量的F127阻碍六方介孔相的形成,降低样品的有序性. F127与十六烷基三甲基溴化铵的摩尔比在0.04-0.08范围内,可以得到有序性好、孔径均一和孔隙率大的单分散纳米介孔二氧化硅MCM--41.

关键词 ：无机非金属材料, 纳米介孔二氧化硅MCM-41, 单

Abstract：Using the cationic surfactant-cetyltrimethylammonium bromide (CTAB) as template, tetraethyl orthosilicate (TEOS) as silica source and nonionic surfactant--triblock copolymer F127 as dispersant, the monodisperse nanosized mesoporous siliceous MCM--41 was prepared by room temperatural synthesis method in basic media. The samples were characterized by techniques such as XRD, TEM, HRTEM, SEM, IR and N$_{2}$ physisorption. In addition, the influences of different molar ratios of F127 to CTAB on mesoporous crystalline structure, surface structure, pore size distribution and the dispersity of nanosized mesoporous siliceous MCM--41 were also systemically studied. The results show that a suitable amount of F127 can greatly improve the ordered structure of pore array, while an excessive amount of F127 will destroy the ordered structure. When the molar ratio of F127 to CTAB was ranged from 0.04 to 0.08, the synthesized samples were nanoparticle, monodispersed, single--pore distributed, huge pore volume and highly ordered mesoporous structure.

Key words： inorganic non-metallic materials nanosized mesoporous siliceous MCM-41 monodisperse triblock copolym

收稿日期: 2004-05-21

ZTFLH:

TB321

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	梁艳
	张劲松
	张军旗
44.8K

链接本文:

https://www.cjmr.org/CN/Y2004/V18/I2/149

1 C.T.Kresge, M.E.Leonowicz, W.J.Roth, Nature, 359, 710(1992)
2 J.S.Beck, J.C.Vartuli, W.J.Roth, J. Am. Chem. Soc., 114, 10834(1992)
3 P.T.Tanev, T.J.Pinnavaia, Science, 267, 865(1995)
4 I.A.Aksay,M.Trau, S.Manne, Science, 273, 892(1996)
5 D.Zhao, P.Yang, G.D.Stucky,Adv.Mater.,10,1380(1998)
6 M.T.Anderson, J.E.Martin, J.Odinek, Microporous Mater.,10(1) ,13(1997)
7 QI Kai, YANG Zhenzhong,YANG Yunxin,Chemical Journal of Chinese Universities,23(2) ,339(2002) (齐凯,杨振忠,杨运信,高等学校化学学报,23(2) ,339(2002) )
8 Q.Huo, J.Feng, Adv. Mater., 9(12) , 974(1997)
9 Q.Huo, J.Feng, F.Schuth, Chem. Mater., 9(1) , 14(1997)
10 Qiang Cai, Zhong Sheng-Luo, Wen Qin-Pang, Chem. Mater.,13, 258(2001)
11 XU Dichun, HAO Xiaochun, ZHU Yihui, Journal of The Chinese Ceramic Society 20(1) ,48(1992) (许迪春,郝晓春,朱宜惠,硅酸盐学报,20(1) ,48(1992) )
12 LI Wei, WANG Hongzhi,GAO lian, Journal of The Chinese Ceramic Society 28(1) , 57(2000) (李蔚,王宏志,高廉,硅酸盐学报,28(1) ,57(2000) )
13 LI Wei, GAO Lian, GUO Jingkun, Journal of Inorganic Materials, 14(1) , 161(1999) (李蔚,高廉,郭景坤,无机材料学报,14(1) ,161(1999) )
14 FANG Xiaolong,YANG Chuanfang, CHEN Jiayong, Journal of The Chinese Ceramic Society,26(6) ,732(1998) (方小龙,杨传芳,陈家镛,硅酸盐学报,26(6) ,732(1998) )
15 SHI Jianlin, GAO Jianhua, LIN Zhuxiang, Journal of The Chinese Ceramic Society,17(5) , 417(1989) (施剑林,高建华,林祖镶,硅酸盐学报,17(5) ,417(1989) )
16 LIU Jifu, WU Houzheng, Journal of The Chinese Ceramic Society,24(1) ,105(1996) (刘继富,吴厚政,硅酸盐学报,24(1) ,105(1996) )
17 BU Lintao, SHAO Qing, DAI Lerong, Chemical Journal of Chinese Universities, 21(6) , 852(2000) (卜林涛,邵青,戴乐蓉,高等学校化学学报,21(6) ,852(2000) )

[1]	宋莉芳, 闫佳豪, 张佃康, 薛程, 夏慧芸, 牛艳辉. 碱金属掺杂MIL125的CO₂ 吸附性能[J]. 材料研究学报, 2023, 37(9): 649-654.
[2]	邵鸿媚, 崔勇, 徐文迪, 张伟, 申晓毅, 翟玉春. 空心球形AlOOH的无模板水热制备和吸附性能[J]. 材料研究学报, 2023, 37(9): 675-684.
[3]	任富彦, 欧阳二明. g-C₃N₄ 改性Bi₂O₃ 对盐酸四环素的光催化降解[J]. 材料研究学报, 2023, 37(8): 633-640.
[4]	刘明珠, 樊娆, 张萧宇, 马泽元, 梁城洋, 曹颖, 耿仕通, 李玲. SnO₂ 作散射层的光阳极膜厚对量子点染料敏化太阳能电池光电性能的影响[J]. 材料研究学报, 2023, 37(7): 554-560.
[5]	李延伟, 罗康, 姚金环. Ni(OH)₂ 负极材料的十二烷基硫酸钠辅助制备及其储锂性能[J]. 材料研究学报, 2023, 37(6): 453-462.
[6]	张敏, 张思倩, 王栋, 陈立佳. 一种镍基单晶高温合金的蠕变组织损伤对再蠕变行为的影响[J]. 材料研究学报, 2023, 37(6): 417-422.
[7]	周章瑞, 吕培森, 赵国旗, 张剑, 赵云松, 刘丽荣. 两种“W替Re”型低成本第二代镍基单晶高温合金的高温持久变形机制[J]. 材料研究学报, 2023, 37(5): 371-380.
[8]	余谟鑫, 张书海, 朱博文, 张晨, 王晓婷, 鲍佳敏, 邬翔. N掺杂生物炭的制备及其对Co²⁺ 的吸附性能[J]. 材料研究学报, 2023, 37(4): 291-300.
[9]	朱明星, 戴中华. SrSc_0.5Nb_0.5O₃ 改性BNT基无铅陶瓷的储能特性研究[J]. 材料研究学报, 2023, 37(3): 228-234.
[10]	刘志华, 岳远超, 丘一帆, 卜湘, 阳涛. g-C₃N₄/Ag/BiOBr复合材料的制备及其光催化还原硝酸盐氮[J]. 材料研究学报, 2023, 37(10): 781-790.
[11]	周毅, 涂强, 米忠华. 制备方法对磷酸盐微晶玻璃结构和性能的影响[J]. 材料研究学报, 2023, 37(10): 739-746.
[12]	孔亚非, 罗兴宏, 李洋, 刘实. 重力对镍基单晶高温合金枝晶生长和微观偏析的影响[J]. 材料研究学报, 2023, 37(10): 770-780.
[13]	陈瑞志, 刘丽荣, 郭圣东, 张迈, 卢广先, 李远, 赵云松, 张剑. 一种6Re/3Ru镍基单晶高温合金微观组织的稳定性和高温持久性能[J]. 材料研究学报, 2023, 37(10): 721-730.
[14]	谢锋, 郭建峰, 王海涛, 常娜. ZnO/CdS/Ag复合光催化剂的制备及其催化和抗菌性能[J]. 材料研究学报, 2023, 37(1): 10-20.
[15]	余超, 邢广超, 吴郑敏, 董博, 丁军, 邸敬慧, 祝洪喜, 邓承继. 亚微米Al₂O₃ 对重结晶碳化硅的作用机制[J]. 材料研究学报, 2022, 36(9): 679-686.

Viewed

Full text

Abstract

Cited

Shared

Discussed