A2017合金半固态压缩的变形机制和成形性能

王顺成;陈彦博;温景林

东北大学

Deformation mechanism and forming property of A2017 alloys during compression in semi--solid state

;;

东北大学

引用本文:

王顺成; 陈彦博; 温景林 . A2017合金半固态压缩的变形机制和成形性能[J]. 材料研究学报, 2004, 18(3): 285-289.

全文: PDF(1565 KB)

摘要: 利用Gleeble--1500热学--力学模拟机, 对A2017半固态合金进行半固态压缩变形实验, 分析了应力-应变曲线和组织变化, 研究了压缩变形机制及成形性能. 结果表明, 用单辊搅拌冷却(SCR)技术制备的A2017半固态合金的组织为细小均匀的非枝晶等轴晶, 二次加热后可转化为均匀的球形晶和共晶液相组成的半固态组织; A2017合金半固态压缩变形的塑性好、变形抗力低; 随着变形温度的升高或者变形速率的降低, 变形的抗力降低. 在稳定的流动变形阶段, A2017合金的半固态变形机制主要由液相流动和固相颗粒的转动与滑动组成, 触变性能稳定, 最大半固态加工变形范围为60\%左右.

关键词 ：材料合成与加工工艺, 半固态金属, 压缩变形, A

Abstract：Semi--solid A2017 alloys were compressed in semi--solid state by means of Gleeble--1500 thermal--mechanical simulator. The microstructures and relationship between the true stress and the true strain were analyzed. The deformation mechanism and forming property of A2017 semi--solid alloys were studied. The results showed that fine and homogeneous non--dendrite microstructures of semi--solid A2017 alloy manufactured by shearing--cooling--rolling (SCR) technology could be obtained and transformed into semi--solid structure which was composed of spherical grains and eutectic liquid through reheating process. The resistance to deformation in semi--solid state decreases as deformation temperature increases or deformation rate decreases. The deformation process of semi--solid A2017 alloy may be divided into four stages. At steady thixotropic deformation stage, the deformation mechanism is liquid flowing, solid particles rotating or sliding, and the thixotropic property is steady. The maximum deformation range is about 60\%.

Key words： synthesizing and processing technics semi-solid metal compression deformation A2017 alloy thixotropi

收稿日期: 2004-07-19

ZTFLH:

TG339

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	王顺成
	陈彦博
	温景林
44.8K

链接本文:

https://www.cjmr.org/CN/Y2004/V18/I3/285

1 XIE Shuisheng, PAN Hongping, DING Zhiyong, Journal of Plasticity Engineering, 9(2) , 1(2002) (谢水生,潘洪平,丁志勇,塑性工程学报,9(2) ,1(2002) )
2 M.C.Flemings, Metall. Trans., 22, 957(1991)
3 D.H.Kirkwood, International Materials Reviews, 39, 173(1994)
4 DONG Jie, CUI Jianzhong, LE Qichi, Mater. Sci. Eng., 345, 234(2003)
5 ZU Lijun, LUO Shoujing, SUN Jiakuan, The Chinese Journal of Nonferrous Metals, 10(S1) , 192(2000) (祖丽君,罗守靖,孙家宽,中国有色金属学报,10(S1) ,192(2000) )
6 SUN Jiakuan, LUO Shoujing, The Chinese Journal of Nonferrous Metals, 9(3) , 493(1999) (孙家宽,罗守靖,中国有色金属报,9(3) ,493(1999) )
7 CHEN Xiaoyang, MAO Weimin, ZHONG Xueyou, Materials for Mechanical Engineering, 22(4) , 25(1998) (陈晓阳,毛卫民,钟雪友,机械工程材料,22(4) ,25(1998) )
8 LIU Dan, CUI Jianzhong, XIA Kenong, Trans. Nonferrous Met. Soc. China, 10(2) , 192(2000)
9 SONG Renbo, KANG Yonglin, YANG Xiongfei, MAO Weimin, YANG Maosheng, Chinese Journal of Materials Research, 14(6) , 591(2000) (宋仁伯,康永林,杨雄飞,毛卫民,杨卯生,材料研究学报,14(6) ,591(2000) )
10 P.K.Seo, S.W.Youn, C.G.Kang, Journal of Materials Processing Technology, 130, 551(2002)
11 C.G.Kang, J.S.Choi, K.H.Kim, Journal of Materials Processing Technology, 88, 159(1999)
12 M.Kiuchi, S.Sugiyama, ISIJ International, 35(6) , 790(1995)
13 WANG Shuncheng, WEN Jinglin, LI Yinglong, CHEN Yanbo, ZHOU Tianguo, Foundry, 52(10) , 740(2003) (王顺成,温景林,李英龙,陈彦博,周天国,铸造,52(10) ,740(2003) )
14 WEN Jinglin, GUAN Renguo, LIU Xianghua, Chinese Journal of Materials Research, 17(1) , 55(2003) (温景林,管仁国,刘相华,材料研究学报,17(1) ,55(2003) )
15 GUAN Rreguo, WEN Jinglin, LIU Xxianghua, Mater. Sci. Tech., 19(4) , 503(2003)
16 T.L.Nguyen, M.Suery, Mater. Sci. Eng., 196, 33(1995)
17 R.Kopp, J.G.Choi, N.Dag, Journal of Materials Processing Technology, 135, 317(2003)
18 E.R.DE Freitas, M.Ferrante, Acta Mater., 49, 3839(2001)

[1]	邵鸿媚, 崔勇, 徐文迪, 张伟, 申晓毅, 翟玉春. 空心球形AlOOH的无模板水热制备和吸附性能[J]. 材料研究学报, 2023, 37(9): 675-684.
[2]	徐利君, 郑策, 冯小辉, 黄秋燕, 李应举, 杨院生. 定向再结晶对热轧态Cu71Al18Mn11合金的组织和超弹性性能的影响[J]. 材料研究学报, 2023, 37(8): 571-580.
[3]	杨栋天, 熊良银, 廖洪彬, 刘实. 基于热力学模拟计算的CLF-1钢改良设计[J]. 材料研究学报, 2023, 37(8): 590-602.
[4]	冯叶, 陈志勇, 姜肃猛, 宫骏, 单以银, 刘建荣, 王清江. 一种NiCrAlSiY涂层对Ti65钛合金板材循环氧化和室温力学性能的影响[J]. 材料研究学报, 2023, 37(7): 523-534.
[5]	雷志国, 文胜平, 黄晖, 张二庆, 熊湘沅, 聂祚仁. 冷轧变形和添加Si对Al-2Mg-0.8Cu(-Si)合金的组织和力学性能的影响[J]. 材料研究学报, 2023, 37(6): 463-471.
[6]	李桥, 牛犇, 张瑞谦, 刘会群, 林国强, 王清. Ta/Zr对Fe-Cr-Al-Mo-Nb合金温轧板材高温组织稳定性的影响[J]. 材料研究学报, 2023, 37(6): 423-431.
[7]	蒋梦蕾, 代斌斌, 陈亮, 刘慧, 闵师领, 杨帆, 侯娟. 选区激光熔化成形尺寸对304L不锈钢点蚀性能的影响[J]. 材料研究学报, 2023, 37(5): 353-361.
[8]	陈志鹏, 朱智浩, 宋梦凡, 张爽, 刘田雨, 董闯. 基于Ti-6Al-4V团簇式设计的超高强Ti-Al-V-Mo-Nb-Zr合金[J]. 材料研究学报, 2023, 37(4): 308-314.
[9]	叶姣凤, 王飞, 左洋, 张钧翔, 罗晓晓, 冯利邦. 兼具高强度、高韧性和自修复性能的环氧树脂改性热可逆聚氨酯[J]. 材料研究学报, 2023, 37(4): 257-263.
[10]	王刚, 杜雷雷, 缪自强, 钱凯成, 杜向博文, 邓泽婷, 李仁宏. 聚多巴胺改性碳纤维增强尼龙6复合材料的界面性能[J]. 材料研究学报, 2023, 37(3): 203-210.
[11]	罗昱, 陈秋云, 薛丽红, 张五星, 严有为. 钠离子电池双层碳包覆Na₃V₂(PO₄)₃ 正极材料的超声辅助溶液燃烧合成及其电化学性能[J]. 材料研究学报, 2023, 37(2): 129-135.
[12]	冯晗旭, 赵连祥, 刘恩泽, 谭政, 宁礼奎, 佟健, 郑志, 李海英, 刘凯. 铬对GH4169母合金中夹杂物的影响[J]. 材料研究学报, 2023, 37(2): 136-144.
[13]	刘志华, 岳远超, 丘一帆, 卜湘, 阳涛. g-C₃N₄/Ag/BiOBr复合材料的制备及其光催化还原硝酸盐氮[J]. 材料研究学报, 2023, 37(10): 781-790.
[14]	邓海龙, 刘兵, 郭扬, 康贺铭, 李明凯, 李永平. 基于内部失效机理预测评估渗碳Cr-Ni齿轮钢的超高周疲劳强度[J]. 材料研究学报, 2023, 37(1): 55-64.
[15]	余超, 邢广超, 吴郑敏, 董博, 丁军, 邸敬慧, 祝洪喜, 邓承继. 亚微米Al₂O₃ 对重结晶碳化硅的作用机制[J]. 材料研究学报, 2022, 36(9): 679-686.

Viewed

Full text

Abstract

Cited

Shared

Discussed