| Dissolution and precipitation of carbide in hot-rolled Inconel alloy 690 |
| HAO Xianchao; CHEN Bo; MA Yingche; GAO Ming; LIU Ku |
| Institute of Metal Research; Chinese Academy of Sciences; Shenyang 110016 |
|
Cite this article:
HAO Xianchao CHEN Bo MA Yingche GAO Ming LIU Ku. Dissolution and precipitation of carbide in hot-rolled Inconel alloy 690. Chin J Mater Res, 2009, 23(6): 668-672.
|
|
|
Abstract The behavior of carbide dissolution and precipitation in hot-rolled Inconel690 has been investigated by means of scanning electron microscopy. Transmission electron microscopy was employed to determine the type of carbide. The results show that more strip like carbide precipitates, identified as M23C6, distribute along grain boundaries in hot-rolled alloy 690 bars, and only few discrete particles present in the matrix. Dissolution temperatures of intergranular and intragranular carbides are 1050 and 1080, respectively. The carbide particles in hot-rolled bar could not fully dissolve and some still existed at grain boundaries for low solution temperature, then these remained carbide particles really hindered the new carbide re-precipitation during the following thermal treatment at 715 . However, to the clean grain boundaries after the carbides are fully dissolved at higher solution temperature, the newly fine and semi-continuous carbide precipitates can formed along the grain boundaries after following thermal treating.
|
|
Received: 02 April 2009
|
|
|
| 1 G.S.Was, Grain boundary chemistry and intergranular fracture in austenitic nickel-base alloys-a review, Corrosion, 46(4), 319(1990)
2 H.Nagano, K.Yomanaka, K.Kobayashi, M.Inoue, Development and manufacturing system of alloy 690 for PWR steam generator tubing, Sumitomo Metals, 40(4), 17(1988)
3 J.M.Sarver, J.R.Crum, W.L.Mankins, Carbide precipitation and SCC behavior of Inconel alloy 690, Corrosion, 44(5), 288(1988)
4 J.J.Kai, M.N.Liu, Effect of heat treatment on the carbide evolution and the chromium depletion along grain boundary of Inconel 690 Alloy, Scripta Metallurgica, 23(1), 17(1989)
5 J.J.Kai, G.P.Yu, C.H.Tsai, M.N.Liu, S.C.Yao, The effects of heat treatment on the chromium evolution, precipitate evolution, and corrosion resistance of Inconel alloy 690, Metallurgy Transaction A, 20, 2057(1989)
6 LI Qiang, ZHOU Bangxin, A study of microstructure of alloy 690, Acta Metallurgica Sinica, 37(1), 8(2001)
(李强, 周邦新, 690合金显微组织研究, 金属学报, 37(1), 8(2001))
7 ZHU Hong, DONG Jianxin, ZHANG Maicang, HU Yaohe, XIE Xishan, Solid-solution effect on microstructure of Inconel690 superalloy, Journal of University of Science and Technology Beijing, 24(5), 511(2002)
(朱红, 董建新, 张麦仓, 胡尧和, 谢锡善, 固溶处理对Inconel690合金组织的影响, 北京科技大学学报, 24(5), 511(2002))
8 LU Yue, QIN Xiubin, The influence of composition and heat treatment on microstructure and material properties of Sandvik Sanicro690(Alloy 690), Boiler Manufacturing, 154(4), 54(1994)
(鲁悦, 秦绪斌, 化学成分合热处理对Sandvik公司690合金的微观结构及材料性能的影响, 锅炉制造, 154(4), 54(1994))
9 GAN Yong, TIAN Zhiling, DONG Hao, FEN Tiao, WANG Xinlin, China Materials Engineering Canon-Steel and Iron Materials Engineering (Beijing, Chemistry Industry Press, 2006) p.490
(干 勇, 田志凌, 董 瀚, 冯 涤, 王新林, 中国材料工程大典第二卷: 钢铁材料工程 (北京, 化学工业出版社, 2006), p.490)
10 LU Shiying, ZHANG Tingkai, KANG Xifan, YANG Changqiang, WANG Xi, Stainless Steels (Beijing, Atomic Energy Press, 1995) p.173
(陆世英, 张廷凯, 康喜范, 杨长强, 王 熙, 不锈钢 (北京, 原子能出版社, 1995) p.173)
11 QIU Shaoyu, SU Xingwan, WEN Yan, YAN Fuguang, YU Yinhua, HE Yanchun, Effect of heat treatment on corrosion resistance of alloy 690, Nuclear Power Engineering, 16(4), 336(1995)
(邱绍宇, 苏兴万, 文燕, 闫福广, 喻应华, 何艳春, 热处理对690合金腐蚀性能影响的实验研究, 核动力工程, 16(4), 336(1995)) |
| No Suggested Reading articles found! |
|
|
Viewed |
|
|
|
Full text
|
|
|
|
|
Abstract
|
|
|
|
|
Cited |
|
|
|
|
| |
Shared |
|
|
|
|
| |
Discussed |
|
|
|
|