Chin J Mater Res  1992, Vol. 6 Issue (4): 308-311    DOI:
Current Issue | Archive | Adv Search |
ATMOSPHERIC CORROSION SURVEY OF A3 STEEL IN INDUSTRIAL CITIES IN LIAONING
HUANG Chunxiao;WU Weitao;SUN Cheng;GAO Gengyu;LUO Jixun;LIU Shourong(Institute of Corrosion and Protection of Metals;Academia sinica)
Cite this article: 

HUANG Chunxiao;WU Weitao;SUN Cheng;GAO Gengyu;LUO Jixun;LIU Shourong(Institute of Corrosion and Protection of Metals;Academia sinica). ATMOSPHERIC CORROSION SURVEY OF A3 STEEL IN INDUSTRIAL CITIES IN LIAONING. Chin J Mater Res, 1992, 6(4): 308-311.

Download:  PDF(280KB) 
Export:  BibTeX | EndNote (RIS)      
Abstract  A two-year survey of atmospheric corrosion of A3 Steel in industrial cities inLiaoning has been made.The results of the field exposure have been analyzed in combinationwith environmental data.The time of wetness and the amount of pollutant SO_2 seem to be
Key words:  atmospheric corrosion      A3 steel      SO_2 pollutant     
Received:  25 August 1992     
Service
E-mail this article
Add to citation manager
E-mail Alert
RSS
Articles by authors

URL: 

https://www.cjmr.org/EN/     OR     https://www.cjmr.org/EN/Y1992/V6/I4/308

1 Ostroff A G,et al 著,王向农等译.腐蚀控制手册.北京:石油工业出版社,1988:156
2 Eadie G R,Johnston R R M.Some Atmospheric Factors Determining Corrosivity in Molburne Area,Proceedings Australia Corrosion Conference.1974:15
3 张安富.材料保护,1989;22(2) :15
4 郑逸平等.环境科学,1991;3(2) :1
5 陈鸿川等.沈阳市区大气腐蚀图,待发
[1] YIN Qi,LIU Miaoran,LIU Yuwei,PAN Chen,WANG Zhenyao. Effect of MgCl2 Deposite on Simulated Atmospheric Corrosion of Zn via Wet-dry Altertnating Corrosion Test[J]. 材料研究学报, 2019, 33(9): 705-712.
[2] Dan ZHANG,Zhenyao WANG. Corrosion Behavior of Zinc Exposed to Salt Lake Area for 48 Months[J]. 材料研究学报, 2019, 33(8): 603-613.
[3] Jin WANG, Qingdan HUANG, Jing LIU, Yaru ZHANG, Chuang QIAO, Long HAO, Junhua DONG, Wei KE. Accelerated Indoor Corrosion of Galvanized Steel in a Simulated Atmospheric Environment of Guangzhou Area[J]. 材料研究学报, 2018, 32(8): 631-640.
[4] Dalei ZHANG, Yuanyuan MIAO, He JING, Xiaohui DOU, Youhai JIN. Effect of Sulphite Deposits on Hydrogen Embrittlement Susceptivity of Hot-dip Galvanized Steel in Marine Atmospheric Environment[J]. 材料研究学报, 2018, 32(7): 533-540.
[5] Dan ZHANG, Zhenyao WANG, Yongzhang ZHOU, Yuwei LIU, Qi YIN, Gongwang CAO. Initial Corrosion Behavior of Galvanized Steel in Atmosphere by Qinghai Salt Lake[J]. 材料研究学报, 2018, 32(4): 255-262.
[6] Shasha WANG,Lang YANG,Yunhua HUANG,Kui XIAO,Xiaogang LI. Initial Corrosion Behavior in Different Atmospheric Environments of 6061Al Alloy Anodized in Boron-sulfuric Acid Solution[J]. 材料研究学报, 2017, 31(1): 49-56.
[7] Ran XU,Yanhua WANG,Jia WANG,Zaijian LIU,Yuan ZHANG. Influence of Spreadability of Seawater Droplet on Electrochemical Characteristics of Carbon Steel[J]. 材料研究学报, 2015, 29(2): 95-100.
[8] JIA Ruiling ZHAI Xiwei YAN Chuanwei WANG Fuhui. Effect of $\beta$ Phase on the Initial Atmospheric Corrosion Behaviour of the Magnesium-Aluminum Alloys by  n-situ
Electrochemical Impendence Spectra
[J]. 材料研究学报, 2010, 24(3): 245-253.
[9] Zhang Dalei Yan LI. Hydrogen permeation of hot-dip galvanized steel exposed to simulated marine atmosphere[J]. 材料研究学报, 2009, 23(6): 592-597.
[10] SUN Cheng;WU Weitao;HUANG Chunxiao;GAO Gengyu;LUO Jixun;LIU Shourong(Institute of Corrosion and Protection of Metals;Academia Sinica). ATMOSPHERIC CORROSION OF ZINC IN LIAONING RURAL AREA[J]. 材料研究学报, 1992, 6(4): 312-314.
No Suggested Reading articles found!