材料研究学报  2013, Vol. 27 Issue (4): 432-438

研究论文 本期目录 | 过刊浏览 |

导电聚苯胺/水性环氧树脂防腐涂料的制备及防腐性能

王娜1, 2 程克奇1 吴航3 王福会2, 3

1. 沈阳化工大学材料科学与工程学院 沈阳 110142 2. 哈尔滨工程大学材料科学与化学工程学院 哈尔滨 150001 3. 中国科学院金属研究所 沈阳 110016

Preparation and Anti-Corrosion Properties of Conductive Polyaniline/Waterborne Epoxy Resin Coatings

WANG Na1, 2 CHENG Keqi1 WU Hang3 WANG Fuhui2, 3*

1. School of Materials Science and Engineering, Shenyang University of Chemical Technology, Shenyang 110142 2. School of Materials Science and Chemical Engineering, Harbin Engineering University, Harbin 150001 3. State Key Laboratory for Corrosion and Protection, Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016

王娜, 程克奇, 吴航, 王福会. 导电聚苯胺/水性环氧树脂防腐涂料的制备及防腐性能[J]. 材料研究学报, 2013, 27(4): 432-438.
. Preparation and Anti-Corrosion Properties of Conductive Polyaniline/Waterborne Epoxy Resin Coatings[J]. Chinese Journal of Materials Research, 2013, 27(4): 432-438.

摘要 相关文章 Metrics 全文: PDF(3908 KB)   摘要: 以导电聚苯胺为防腐颜料制备水性环氧防腐涂层, 用光学显微镜观测聚苯胺在水性环氧中的分散性, 用电化学阻抗谱(EIS)、极化曲线分析(LSV)、盐雾试验以及X衍射光谱(XRD)表征涂层的防腐性能, 研究了聚苯胺(PANI)添加量对水性环氧树脂涂层防腐性能的影响。结果表明, 在涂层中引入导电聚苯胺使涂层具有一定的导电性。随着聚苯胺添加量的增加涂层导电性提高, 将金属腐蚀产生的电子导到涂层与溶液的界面上, 隔离阴阳极间的反应, 形成完整的金属表面氧化膜。同时, 聚苯胺对金属离子的螯合作用和对氧气的屏蔽提高了涂层的抗“闪锈”能力和防腐效果。但是, 聚苯胺添加量过大(达到0.8%)使涂层后期的屏蔽腐蚀离子效果明显降低, 使防腐作用主要依赖氧化膜, 涂层综合防腐效果降低。聚苯胺添加量(质量分数)为0.6 %时聚苯胺在水性环氧中分散效果好, 金属表面涂层的氧化膜均匀, 具有最好的抗“闪锈”能力和防腐性能。 Abstract：The waterborne anti-corrosion paint was prepared by introducing the anti-corrosion pigment of conductive polyaniline (PANI) to the waterborne epoxy. Adding quantity (mass fraction) of PANI was 0, 0.2%, 0.4%, 0.6%, 0.8%, respectively. The dispersion and anti-corrosion effect were characterized with optical microscopic, electrochemical impedance spectroscopy (EIS), polarization curve analysis (LSV), X-ray diffraction (XRD), and salt spray test. The effects of the quantity of PANI on the anti-corrosion property of the waterborne anti-corrosion paint were investigated. The anodic and cathodic reaction can be insulated because of the suitable PANI adding, and the metal chelating substance and the shielding effect of oxygen are helpful. Metal oxide film formed intactly and the coating “flash” rust resistance and anti-corrosion effect can be improved. But when the adding amount of PANI was 0.8%, the effect of anti-corrosion decreased because the shielding the corrosion ions of the epoxy film decreased. The anti-corrosion property is the best when the quantity of PANI was 0.6%. The PANI can improve the quality of the oxidation film, and overcome the “flash rust” problem effectively.      ZTFLH:  TB304   服务 把本文推荐给朋友 加入引用管理器 E-mail Alert RSS 作者相关文章 44.8K 链接本文: https://www.cjmr.org/CN/      或      https://www.cjmr.org/CN/Y2013/V27/I4/432 [1] 李玉峰, 张念飞, 刘丽爽, 赵甜甜, 高文博, 高晓辉. 含磷石墨烯的制备及复合涂层的耐蚀性能[J]. 材料研究学报, 2022, 36(12): 933-944. [2] 王娜, 陈俊声, 王树伟, 张静. 氨基化氧化石墨烯在水性防腐防火一体化涂料中的应用[J]. 材料研究学报, 2018, 32(10): 721-729. [3] 许璐, 车淳山, 孔纲, 王彦启, 曹祖军. 硅酸钠溶液的模数对Zn-5%Al镀层上硅酸盐转化膜的影响[J]. 材料研究学报, 2018, 32(8): 607-615. [4] 高晓辉, 景晓燕, 李玉峰, 祝晶晶, 祁实. 镁锂合金表面水性SiO2@PANI/VTMS涂层的防腐蚀性能[J]. 材料研究学报, 2018, 32(1): 42-50. [5] 孙京丽, 邹丹, 金晶, 李莉, 刘海英. 三种常用不锈钢的耐局部腐蚀性能[J]. 材料研究学报, 2017, 31(9): 665-671. [6] 吴晓晓, 孔纲, 孙子文, 车淳山. 热浸镀Galfan表面镧盐转化膜的生长和耐腐蚀性能的研究[J]. 材料研究学报, 2016, 30(4): 269-276. [7] 刘明明, 刘福春, 韩恩厚, 唐囡, 万军彪, 邓静伟. 纳米碳酸钙浓缩浆对环氧涂层耐蚀性的影响*[J]. 材料研究学报, 2013, 27(4): 425-431. [8] 李承波,刘胜胆,王国玮,金亚楠,张新明. 冷却速率对Al-Zn-Mg-Cu合金厚板剥落腐蚀的影响*[J]. 材料研究学报, 2013, 27(3): 259-267. [9] 盛敏奇,钟庆东, 吕臣凯, 万康. 施加超声波电沉积制备Co-Ni合金层*[J]. 材料研究学报, 2013, 27(3): 267-272. [10] 盛敏奇 许继芳 万康, 吕臣凯. 低碳钢表面Fe-Ni合金层的制备及耐腐蚀性能[J]. 材料研究学报, 2013, 27(2): 183-188. [11] 丁锐 李相波, 王佳, 许立坤. 冷喷涂Cu-Cu2O涂层在海水中的电化学行为[J]. 材料研究学报, 2013, 27(2): 212-218. [12] 葛延峰 蒋百灵 李育磊 杨志远. 镁合金表面微弧氧化--SiO2复合膜层的微观结构和耐蚀性[J]. 材料研究学报, 2011, 25(1): 79-83. [13] 李振华 盛敏奇 钟庆东 王毅 吴红艳 杜海龙. 基体表面粗糙度对H13钢板表面镀铬层的影响[J]. 材料研究学报, 2010, 24(5): 455-463. [14] 田晓 贾清 崔玉友 杨锐. TiAl合金防护涂层先驱溶胶的热分解和晶化过程[J]. 材料研究学报, 2010, 24(5): 483-486. [15] 杨巍 蒋百灵 时惠英 鲜林云. 镁合金微弧电泳复合膜层的微观结构和抗腐蚀性能[J]. 材料研究学报, 2009, 23(4): 421-425. Viewed Full text Abstract Cited   Shared      Discussed