材料研究学报  1991, Vol. 5 Issue (6): 472-476

研究论文 本期目录 | 过刊浏览 |

三源真空共蒸发沉积 CuInSe_2薄膜

魏晋云;廖华;王东城

云南师范大学太阳能研究所;云南师范大学;云南师范大学

VACUUM Co-EVAPORATED DEPOSITION FOR CuInSe_2 THIN FILM BY THREE-SOURCES PROCESS

WEI Jinyun LIAO Hua WANG Dongcheng (Yunnan Normal University)

魏晋云;廖华;王东城. 三源真空共蒸发沉积 CuInSe_2薄膜[J]. 材料研究学报, 1991, 5(6): 472-476.
, , . VACUUM Co-EVAPORATED DEPOSITION FOR CuInSe_2 THIN FILM BY THREE-SOURCES PROCESS[J]. Chin J Mater Res, 1991, 5(6): 472-476.

摘要 参考文献 相关文章 Metrics 全文: PDF(617 KB)   摘要: 用三源真空共蒸发沉积CuInSe_2。调节三源的配方及蒸发速率,控制薄膜的组分,获得了具有单相黄铜矿结构的多晶CuInSe_2薄膜。发现适当的热处理对薄膜的成相是必需的。研究了薄膜组分、结构、光学和电学性质与工艺条件的关系。 关键词 ： 太阳电池,  CuInSe_2薄膜,  真空蒸发     Abstract：Thin films of CuInSe_2 have been co-evaporated in vacuum bythree-sources process.The compositions of the films have been controlled by ratio of theelements in the three sources and temperature of the three sources.Satisfactary compositionand single chalco Key words： solar cell    CuInSe_2 film    vacuum evaporation 收稿日期: 1991-12-25      基金资助:国家自然科学基金,5880101 服务 把本文推荐给朋友 加入引用管理器 E-mail Alert RSS 作者相关文章 魏晋云 廖华 王东城 44.8K 链接本文: https://www.cjmr.org/CN/      或      https://www.cjmr.org/CN/Y1991/V5/I6/472 1 Mickelsen R A,Stanbery B J et al.Proc 19th IEEE Photovoltaic Specialists Conf,1987:744 2 Elliott E,Tomlinson R D et al.Thin Solid Films,1974;20:S25 3 White F R,Clark A H et al.J Appl Phys,1979;50:544 4 Piekoszewski J,Loferski J J et al Proc 14th IEEE Photovoltalc Specialist Conf 1980:980 5 Pamplin B,Fjeglson R S.Thin Solid Films,1979;60:141 6 Padan G K et al.Solar Energy Mat,1986;13:291 7 Gary Hodes.David Cahen.Solar Cells,1986;16:245 8 Sun L Y,Kazerski L L et al.J Vac Sci Technol,1978;15:265 9 Mickelson R A,Chen W S.IEEE Trans,Electron Devices,1984;31:542 10 Neelkanth G Dhere,Cristina Lourenco M et al.Solar Cellls,1986;16:369 11 Denton R E,Campbell R D et al J Phys,1972;5:852 12 Horig W,Neumann H.Thin Solid Films,1978;48:67# [1] 欧阳良琦,赵明,庄大明,孙汝军,郭力,李晓龙,曹明杰. 退火温度对铜铟镓硒薄膜电学性能的影响[J]. 材料研究学报, 2014, 28(10): 745-750. [2] 谢敏 庄大明 刘江 郭力 宋军. 硫化温度对铜锌锡硫薄膜特性的影响*[J]. 材料研究学报, 2013, 27(2): 126-130. [3] 奚小网 胡林华 刘伟庆 戴松元. 基于4--叔丁基吡啶的染料敏化太阳电池中电子传输研究[J]. 材料研究学报, 2011, 25(6): 613-617. [4] 彭英才 傅广生. 量子点太阳电池的探索[J]. 材料研究学报, 2009, 23(5): 449-457. Viewed Full text Abstract Cited   Shared      Discussed