MOLTEN NaCl-(Na,K)_2SO_4 INDUCED HOT CORROSION OF Fe-Cr ALLOYS

ZHANG Jianqing;ZENG Chaoliu;WU Weitao(Corrosion Science Laboratory;Institute of Corrosion and Protection of Metals;Academia Sinica)

ZHANG Jianqing;ZENG Chaoliu;WU Weitao(Corrosion Science Laboratory;Institute of Corrosion and Protection of Metals;Academia Sinica). MOLTEN NaCl-(Na,K)_2SO_4 INDUCED HOT CORROSION OF Fe-Cr ALLOYS. Chin J Mater Res, 1992, 6(5): 375-380.

Abstract References Related Articles Recommended Metrics Download:  PDF(795KB)  Export:  BibTeX | EndNote (RIS)       Abstract  The electrochemical methods were employed to study hot corrosion of Fe-Cr al-loys in molten NaCl-(Na,K)_2SO_4 at 800℃,and the reaction products were examined bymetallographic and EPMA techniques.The experimental results indicate that the addition of Crto Key words:  Fe-Cr alloys      hot corrosion      NaCl-(Na      K)_2SO_4      oxidation-sulfidation      fluxing      Received:  25 October 1992      Service E-mail this article Add to citation manager E-mail Alert RSS （） Articles by authors URL:  https://www.cjmr.org/EN/     OR     https://www.cjmr.org/EN/Y1992/V6/I5/375 1 张允书,李选明,史良权等.中国腐蚀与防护学报,1991;11(1) :17 2 Trafford D N H,Nhittle D P.Corrosion Science,1980;20:497 3 Trafford D N H,Nhittle D P.Corrosion Science,1980;20:509 4 牛焱,吴维(山文),张鉴清等.中国腐蚀与防护学报,1991;11(3) :233 [1] Yaru SUN,Suai ZHAO,Daile ZHANG,Qing HE. Effect of Cr and Al on Hot Corrosion Behavior of Low Thermal Expansion Thermo-span Superalloy at 650℃[J]. 材料研究学报, 2014, 28(8): 627-632. [2] WANG Xinyue XIN Li WEI Hua ZHU Shenglong WANG Fuhui. Influence of Al–Si Coating on Oxidation and Hot Corrosion of a Nickel–base Super–alloy M951[J]. 材料研究学报, 2012, 26(6): 643-651. [3] PAN Taijun HU Jing NIU Yan. Degradation of the chromia on Fe--15Cr--xAl alloy induced by KCl--ZnCl2 deposits[J]. 材料研究学报, 2009, 23(4): 347-351. [4] SHEN Jianianl; ZHOU Longjiang; LI Tiefan(Institute of Materials; Shanghai University; Shanghai 200072; 2. State Key Lab. of Corrosion science; Institute of Corrosion and Protection of Metals; The Chinese Academy of Science ). EFFECT OF WATER VAPOR ON HIGH TEMPERATURE OXIDATION OF Fe-Cr ALLOYS[J]. 材料研究学报, 1998, 12(2): 128-132. [5] ZENG Chaoliu Zhang Jianqing Wu Weitao (Institute of Corrosion and Protection of Metals;Corrosion Science Lab;Chinese Academy of Sciences)Li Dong (Institute of Metals Research;Chinese Academy of Sciences). HOT CORROSION OF Ti_3Al INTERMETALLIC COMPOUND[J]. 材料研究学报, 1993, 7(5): 376-379. [6] ZHANG Song YAN Yonggen ZHU Jingpu (Shenyang Polytechnic University)WANG Maocai WU Weitao (Institute of Corrosion and Protection of Metals;Chinese Academy of Sciences). STUDY ON THE MICROSTRUCTURE AND SALT-COATING HOT CORROSION RESISTANCE OF LASER CLADDING Co-BASE ALLOY[J]. 材料研究学报, 1993, 7(4): 304-308. No Suggested Reading articles found! Viewed Full text Abstract Cited   Shared      Discussed