NON-STEADY SELF-ORGANIZATION DURING SINGLE CRYSTAL INITIAL GROWTH OF SUPERALLOY DD3 UNDER HIGH TEMPERTURE GRADIENT DIRECTIONAL SOLIDIFICATLON CONDITION

WEI Pengyi; LI Jianguo; FU HengZhi(Northwestern Polytechnical University)

WEI Pengyi; LI Jianguo; FU HengZhi(Northwestern Polytechnical University). NON-STEADY SELF-ORGANIZATION DURING SINGLE CRYSTAL INITIAL GROWTH OF SUPERALLOY DD3 UNDER HIGH TEMPERTURE GRADIENT DIRECTIONAL SOLIDIFICATLON CONDITION. Chin J Mater Res, 1996, 10(6): 580-586.

Abstract References Related Articles Recommended Metrics Download:  PDF(1821KB)  Export:  BibTeX | EndNote (RIS)       Abstract   Microstructure evolution and selection in initial transient zone of single crystal superalloyDD3 was investigated with high temperature gradient directional solidification equipment ZMLMC (temperature gradient at solid-liquid interfaCe up to 1300K/cm) wit Key words:  : single crystal superalloy non-steady self-organization directional solidificationCorrespondent: WEI Pengyi      State Key Laboatory of Solidifcation Processing      Northwestern Polytechnical University      Xi'an 710072      Received:  25 December 1996      Service E-mail this article Add to citation manager E-mail Alert RSS （） Articles by authors URL:  https://www.cjmr.org/EN/     OR     https://www.cjmr.org/EN/Y1996/V10/I6/580 1王祖锦．亚快速定向凝固界面形态演化和选择,[博士学位论文],西北工业大学,1993．72Huangweidong,WeiQiuming,ZhouYaoheJCrystGrowth1990,100:263CaroliB,CarolicC,Ramirez-Piscina．JCrystGrowth,1993,132:3774KurzW,FisherDJ著．毛协民等译．凝固原理,西安:西北工业大学出版社,1987:575李建国,储双杰,刘忠元等．机械工程学报,1992,28(86):34 No related articles found! No Suggested Reading articles found! Viewed Full text Abstract Cited   Shared      Discussed