SOLIDIFICATION OF HIGHLY UNDERCOOLED Al-Mn-Si ALLOY

GUO Junqing;LI Qingchun(Harbin Institute of Technology)

Cite this article:

GUO Junqing;LI Qingchun(Harbin Institute of Technology). SOLIDIFICATION OF HIGHLY UNDERCOOLED Al-Mn-Si ALLOY. Chin J Mater Res, 1990, 4(5): 404-408.

Download:

PDF(792KB)
Export: BibTeX | EndNote (RIS)

Abstract Wrapped up by quarz and treated by heating—cooling cycle,highlyundercooled Al-25.44 Mn-17.15Si melt was obtained.Experiment results show that thephase seperation from liquid appears three times when the alloy solidifies.It is found byX-ray diffraction and

Key words: highly undercooled solidification quasicrystal Al-Mn-Si alloy

Received: 25 October 1990

	Service

	E-mail this article
	Add to citation manager
	E-mail Alert
	RSS
	（）
	Articles by authors

URL:

https://www.cjmr.org/EN/ OR https://www.cjmr.org/EN/Y1990/V4/I5/404

1 H Yamane,K Kimura,T Shibuya,S Takeuchi.Production of AI-Based Ternary and Quaternary Icosahedral Phases,Proceedings of International Workshop on Quasicrystals,Beijing,China,Sept.,1987#

[1]	DONG Chuang; FU Yaochun; WANG Dehe; XU Weiping;SONG Meili;WANG Yingmin(Dalian University of Technology)(Professor. Department of Materials Engineering; Dalian Univesity of Technology. Dalian 116024). A NEW QUASICRYSTAL-RELATED Al-Cu PHASE[J]. 材料研究学报, 1995, 9(2): 107-110.
[2]	DONG Chuang (Dalian University of Technology)(Correspondent:DONG Chuang; Professor; Department of Materials Engineering; Dalian 116024; P. R. China). THE FORMATION MECHANISM, PROPERTIES AND APPLICATION POTENTIALS OF QUASICRYSTALLINE MATERIALS[J]. 材料研究学报, 1994, 8(6): 482-490.

No Suggested Reading articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed