热应变脆化对低碳钢解理特征应力的影响

类维生;姚枚

清华大学;哈尔滨工业大学

EFFECT OF HOT STRAININGEMBRITTLEMENT ON CLEAVAGE CHARACTERISTICSTRESS S_(co) OF 16Mn STEEL

LEI Weisheng; YAO Mei(Tsinghua Universily)(Harbin Institute Of Technolgy)

类维生;姚枚. 热应变脆化对低碳钢解理特征应力的影响[J]. 材料研究学报, 1994, 8(2): 142-143.
, . EFFECT OF HOT STRAININGEMBRITTLEMENT ON CLEAVAGE CHARACTERISTICSTRESS S_(co) OF 16Mn STEEL[J]. Chin J Mater Res, 1994, 8(2): 142-143.

摘要 参考文献 相关文章 Metrics 全文: PDF(151 KB)   摘要: 在工作[1]的基础上,研究了热应变脆化处理后16Mn钢的低温拉伸断裂行为表明在250℃进行的预应变量为8%的热应变脆化处理没有改变解理特征应力的数值 关键词 ： 16Mn钢,  低温性能,  热应变脆化,  解理断裂     Abstract：The low-temperature fractrure behavior of 16Mn steel suffered from the hot-strainingembrittlement (HSE) with a strain of about 8%. has been investigated, It is indicated that the by is increasedand the cleavage characteristic stress Sco is hardly affected Key words： 16Mn steel; low-temperature properties; hot-straining embrittlement (HSE); cleavage fracture 收稿日期: 1994-04-25      基金资助:国家自然科学基金 服务 把本文推荐给朋友 加入引用管理器 E-mail Alert RSS 作者相关文章 类维生 姚枚 44.8K 链接本文: https://www.cjmr.org/CN/      或      https://www.cjmr.org/CN/Y1994/V8/I2/142 1类维生,郭永良,跳枚,田锡唐．材料科学进展,1992;6(4):3012YaoM,HeYK,LiDM,ZhouCZ,In:ValIuriSRetaleds．ProceedingsofICF6,Oxford:PergamonPress,1984:14233类维生,结构钢冷脆的解理特征应力理论,哈尔滨工业大学博士学位论文,1992． [1] 钟盛文, 张华军, 姚文俐, 张骞, 付宇坤, 唐小冬. LiNi0.5Mn0.5-xCoxO2(0≤x≤0.12)正极材料的制备及其电化学性能[J]. 材料研究学报, 2018, 32(7): 487-494. [2] 陈亮山;赵铁民;斯重遥;陈怀宁. 爆炸冲击提高16Mn钢焊缝疲劳极限的机理[J]. 材料研究学报, 1994, 8(3): 233-236. [3] 类维生;郭永良;姚枚;田锡唐. 应变速率对低碳钢解理特征应力的影响[J]. 材料研究学报, 1992, 6(4): 301-303. Viewed Full text Abstract Cited   Shared      Discussed