8mol%CeO_2-ZrO_2中的贝氏体相变

徐祖耀;江伯鸿;漆玄;吕伟;周伟敏;钟家湘

上海交通大学;北京理工大学

BAINITIC TRANSFORMATION IN 8mol%CeO_2-ZrO_2

HSU T Y(XU Zuyao); JIANG Bohong; QI Xuan; LU Wei; ZHOU Weimin(Shanghai Jiao Tong University)ZHONG Jiaxiang(Beijing Institute of Technology)

徐祖耀;江伯鸿;漆玄;吕伟;周伟敏;钟家湘. 8mol%CeO_2-ZrO_2中的贝氏体相变[J]. 材料研究学报, 1995, 9(4): 338-344.
, , , , , . BAINITIC TRANSFORMATION IN 8mol%CeO_2-ZrO_2[J]. Chin J Mater Res, 1995, 9(4): 338-344.

摘要 参考文献 相关文章 Metrics 全文: PDF(541 KB)   摘要: 测定8mol%CeO2-ZrO2在连续冷却中变温t→m的Ms,在Ms以上及以下的等温相变动力学曲线和相变产物的点阵常数等.温相变产物(贝氏体)的点阵常数小于变温马氏体的点阵常数.参照金属材料中的贝氏体相变,建议8mol%CeO2—ZrO2的等温相变为扩散过程控制的贝氏体相变.贝氏体可能在母相晶界形核. 关键词 ： 8mol%CeO_2-ZrO_2,  t→m相变,  贝氏体相交     Abstract：The Ms of the athermal transformation t→m on continuous cooling, the kinetics curve of isothermal transformations above and below Ms and the lattice parameters of the transformation product are measured for 8mol% CeO2-ZrO2. The lattice parameter of the is Key words： 8mol%CeO_2-ZrO_2 transformation t→m bainitic transformation 收稿日期: 1995-08-25      服务 把本文推荐给朋友 加入引用管理器 E-mail Alert RSS 作者相关文章 徐祖耀 江伯鸿 漆玄 吕伟 周伟敏 钟家湘 44.8K 链接本文: https://www.cjmr.org/CN/      或      https://www.cjmr.org/CN/Y1995/V9/I4/338 1NakanishiN,ShigematsuT．MaterTransJIM,1991;32(8):7782NakanishiN,ShigematsuT．MaterTransJIM,1992;33(3):3183SatoT,ShimadaM．AmerCeramSocBull,1985;64(10):13824JiangB,TuT,HsuTY(XuZuyao)etal．MaterResSocSympProc,1992;246:2135XuZuyao(HsuTY)．ChineseJournalofMaterialsResearch,1994;8(1):416WuMH,MuddleBC,WaymanCM．ActaMetall,1988;36(8):20957TadakiT,UyedaT,ShimizuK．MaterTransJIM,1989;30(2):1178CliffG,HasanF,LorimerGW,KikuchiM．MetallTrans．1990;21A(4):8319WuMH,WaymanCM．ProcInterConfMartensiticTransformations-86,JapInstMetals,1987;61910NakataY,TadakiT,ShimizuK．MaterTransJIM,1989;30(2):10711TakezawaK,SatoS．MetallTrans,1990:21A(6):154112HamadaY,WuMH,WaymanCM．MaterTransJIM,1991;32(8):74713TadakiT,CaiJQ,ShimizuK．MaterTransJIM,1991;32(8):75714HsuTY(XuZuyao),ZhouXW．ActaMetall．Sinica(EnglishEdition),1992;SerA,5(1):46515HsuTY(XuZuyao),ZhouXW．MetallTrans,1994;25A(12):255516HsuTY(XuZuyao),MouYiwen．ActaMetall,1984;32(9):146917MouYiwen,HsuTY(XuZuyao)．MetallTrans,1988;19A(7):169518HsuTY(XuZuyao),ZhouXW．ActaMetall．1989;37(11):309519HsuTY(XuZuyao),ZhouXW．ActaMetallMater,1991;39(11):261520JiangL,LuW,JiangB,HsuTY(XuZuyao)．TransNon-FerrousMetalsSoc．China(EnglishEdition),1991;1(1):5721ChenWeizhong,HsuTY(XuZuyao),ChenShuchuan,ZhangJihua．ActaMetallMater,1990;38(11):233722LuW,JiangB,HsuTY(XuZuyao)．ScriptaMetallMater,1992;27(7):86123HsuTY(XuZuyao)．MetallTrans,1990;21A(4):81124HsuTY(XuZuyao)．MaterSciProgress(China),1988;2(3):125HayakawaM,OkaM．ActaMetall,1989;37(8):2229 [1] No Author. 贝氏体相变的三面观[J]. 材料研究学报, 1994, 8(2): 97-119. Viewed Full text Abstract Cited   Shared      Discussed