一种低Re二代单晶高温合金长期时效后的性能
Microstructure-property Evolution in a Low-rhenium Second-generation Single Crystal Superalloy Following Long-term Aging
一种低Re二代单晶高温合金长期时效后的性能 |
| 付芸迪, 申健, 黄亚奇, 卢玉章, 王栋 |
|
Microstructure-property Evolution in a Low-rhenium Second-generation Single Crystal Superalloy Following Long-term Aging |
| FU Yundi, SHEN Jian, Huang Yaqi, LU Yuzhang, WANG Dong |
| 图14 完全热处理态和长期时效500 h、1000 h合金的持久宏观断口 |
| Fig.14 Macroscopic fracture surfaces of the alloy after stress rupture testing (a, b) fully heat-treated condition, (c, d) long-term aged for 500 h, (e, f) long-term aged for 1000 h |
|
|