δ-铁素体含量对高SiN奥氏体不锈钢焊缝性能的影响 |
||||||||||||||||
| 杨景清, 董文超, 陆善平 | ||||||||||||||||
|
Effect of δ-ferrite Content on Resistance to Cracking and Nitric Acid Corrosion of Weld Joints for High SiN Austenitic Stainless Steel |
||||||||||||||||
| YANG Jingqing, DONG Wenchao, LU Shanping | ||||||||||||||||
| 表3 FISCO实验后焊缝金属的裂纹长度、焊缝长度和裂纹率 |
||||||||||||||||
| Table 3 Crack length, weld length, and crack rate of weld metal after FISCO test |
||||||||||||||||
|
||||||||||||||||