第一壁自钝化W-Cr-Zr合金的氧化行为和氧化层结构
Oxidation Behavior of Self-passivated W-Cr-Zr Alloys as the First Wall Candidate Material
第一壁自钝化W-Cr-Zr合金的氧化行为和氧化层结构 |
| 吴玉程, 左彤, 谭晓月, 朱晓勇, 刘家琴 |
|
Oxidation Behavior of Self-passivated W-Cr-Zr Alloys as the First Wall Candidate Material |
| WU Yucheng, ZUO Tong, TAN Xiaoyue, ZHU Xiaoyong, LIU Jiaqin |
| 图6 表面粗糙度不同的W-Cr-Zr合金在1000 ℃氧化20 h后氧化层的截面、氧化层厚度与样品氧化前表面粗糙度的关系以及样品氧化后的表面粗糙度 |
| Fig.6 Cross section of oxide scale of W-Cr-Zr alloy with different roughness surfaces after oxidation at 1000 oC for 20 h (a~d), the relationship between the thickness of oxide scale and surface roughness of samples before oxidation (e) and the surface roughness of oxide scales (f) |
|
|