第一壁自钝化W-Cr-Zr合金的氧化行为和氧化层结构
Oxidation Behavior of Self-passivated W-Cr-Zr Alloys as the First Wall Candidate Material
(a) Ra = 0.64 μm, (b) Ra = 0.51 μm, (c) Ra = 0.41 μm, (d) Ra = 0.24 μm
第一壁自钝化W-Cr-Zr合金的氧化行为和氧化层结构 |
| 吴玉程, 左彤, 谭晓月, 朱晓勇, 刘家琴 |
|
Oxidation Behavior of Self-passivated W-Cr-Zr Alloys as the First Wall Candidate Material |
| WU Yucheng, ZUO Tong, TAN Xiaoyue, ZHU Xiaoyong, LIU Jiaqin |
| 图2 表面粗糙度不同的W-Cr-Zr合金在1000 ℃氧化2 min后氧化层表面的形貌 |
| Fig.2 Surface morphology of W-Cr-Zr alloy with different surface roughness after oxidation at 1000 oC for 2 min (a) Ra = 0.64 μm, (b) Ra = 0.51 μm, (c) Ra = 0.41 μm, (d) Ra = 0.24 μm |
|
|