原位小冲头压缩速率对X65管线钢氢脆敏感性的影响
Effect of Compression Rate on Hydrogen Embrittlement Sensitivity of X65 Pipeline Steel Based on in-situ Small Punch Test
原位小冲头压缩速率对X65管线钢氢脆敏感性的影响 |
| 吴晓祺, 万红江, 明洪亮, 王俭秋, 柯伟, 韩恩厚 |
|
Effect of Compression Rate on Hydrogen Embrittlement Sensitivity of X65 Pipeline Steel Based on in-situ Small Punch Test |
| WU Xiaoqi, WAN Hongjiang, MING Hongliang, WANG Jianqiu, KE Wei, HAN En-Hou |
| 图11 压缩速率为1 mm·min-1条件下在4 MPa氮气及氢气环境中试样的破裂截面图 |
| Fig.11 Cross-sectional diagram of specimen fracture under a compression rate of 1 mm·min-1 in nitrogen environment (a) and hydrogen environment (b) at 4 MPa |
|
|