PHCN准固态电解质的制备和性能
Synthesis and Performance of a Novel Quasi-solid-state Electrolyte PHCN Based on Polyvinylidene Fluoride-hydrogenated Acrylate Incorparated with Mesoporous Spherical g-C3N4
PHCN准固态电解质的制备和性能 |
| 梁洪华, 陈江超, 郑文育, 吴海宁, 黄亦聪, 易卓彦, 庞大志, 蒋坤朋, 朱归胜, 徐华蕊 |
|
Synthesis and Performance of a Novel Quasi-solid-state Electrolyte PHCN Based on Polyvinylidene Fluoride-hydrogenated Acrylate Incorparated with Mesoporous Spherical g-C3N4 |
| LIANG Honghua, CHEN Jiangchao, ZHENG Wenyu, WU Haining, HUANG Yicong, YI Zhuoyan, PANG Dazhi, JIANG Kunpeng, ZHU Guisheng, XU Huarui |
| 图4 温度为30 ℃时Nyquist图、阿伦尼乌斯曲线、活化能曲线、PHCN-3在30 ℃极化前后的电池极化曲线和阻抗图、PHCN-3和PVDF-HFP准固态电解质在30 ℃、扫描速率为10 mV·s-1的LSV曲线 |
| Fig.4 Nyquist plots at 30 oC (a), Arrhenius plots (b), activation energy plots (c), chromoamperometry curve and corresponding Nyquist plots before and after polarization for PHCN-3 at 30 oC (d), LSV curves of PHCN-3 and PVDF-HFP quasi-solid electrolytes at 30 oC with a scan rate of 10 mV·s-1 (e) |
|
|