四方相氧化钇稳定氧化锆热障涂层的热循环和热冲击性能及其失效机理
Thermal Cycling and Flame Thermal Shocking Failure Mechanism of Tetragonal Yttria-stabilized Zirconia TBCs Prepared on High Temperature Alloys by Suspension Plasma Spraying
四方相氧化钇稳定氧化锆热障涂层的热循环和热冲击性能及其失效机理 |
| 黄迪, 牛云松, 李帅, 董志宏, 鲍泽斌, 朱圣龙 |
|
Thermal Cycling and Flame Thermal Shocking Failure Mechanism of Tetragonal Yttria-stabilized Zirconia TBCs Prepared on High Temperature Alloys by Suspension Plasma Spraying |
| HUANG Di, NIU Yunsong, LI Shuai, DONG Zhihong, BAO Zebin, ZHU Shenglong |
| 图3 1100℃热循环失效后的陶瓷层、完整TGO区域和柱内结构的高倍微观截面照片 |
| Fig.3 Cross-section images of TC (a), intact TGO region (b) and inter-column high-magnification (c, d) after failure at 1100oC thermal cycling |
|
|