轧制温度对Mg-4Zn-1Mn-1.2Ce合金板材微观组织及力学/导热性能的影响

崔捷, 李旭东, 杜宪, 李淑波, 杜文博

Effect of Rolling Temperature on Microstructure Evolution and Mechanical/Thermal Properties of Mg-4Zn-1Mn-1.2Ce Alloy Sheet

CUI Jie, LI Xudong, DU Xian, LI Shubo, DU Wenbo

表1 图3中A-H点的EDS分析结果(原子分数，%)

Table 1 EDS analysis of the A-H points in Fig.3 (%, atom fraction)

Point Mg Zn Mn Ce A 80.56 15.27 0.56 3.61 B 62.12 2.78 18.32 16.78 C 73.58 20.41 0.59 5.42 D 43.03 0.86 54.05 2.06 E 34.56 0.80 64.32 0.32 F 66.44 25.70 0.90 6.96 G 81.70 13.67 0.55 4.08 H 52.37 0.60 46.93 0.10