钛合金的超高周疲劳滑移-解理竞争失效机制
Evaluation of Slip-cleavage Competition Failure Mechanisms for Titanium Alloys Induced by Microstructure in Very-high-cycle Fatigue Regime
钛合金的超高周疲劳滑移-解理竞争失效机制 |
| 杨溥, 邓海龙, 康贺铭, 刘杰, 孔建行, 孙宇凡, 于欢, 陈雨 |
|
Evaluation of Slip-cleavage Competition Failure Mechanisms for Titanium Alloys Induced by Microstructure in Very-high-cycle Fatigue Regime |
| YANG Pu, DENG Hailong, KANG Heming, LIU Jie, KONG Jianhang, SUN Yufan, YU Huan, CHEN Yu |
| 图12 与σmax有关的三种失效模式的失效概率随a晶粒尺寸的变化情况 |
| Fig.12 Change of failure probability with a grain size for the three failure modes related to σmax (a) surface slip failure (b) surface cleavage failure (c) internal cleavage failure |
|
|