铝粉粒径和热压温度对15%SiC/2009Al复合材料力学性能的影响
Effect of Aluminum Powder Size and Temperature on Mechanical Properties of Hot Pressed 15%SiC/2009Al Composite
铝粉粒径和热压温度对15%SiC/2009Al复合材料力学性能的影响 |
| 边鹏博, 韩修柱, 张峻凡, 朱士泽, 肖伯律, 马宗义 |
|
Effect of Aluminum Powder Size and Temperature on Mechanical Properties of Hot Pressed 15%SiC/2009Al Composite |
| BIAN Pengbo, HAN Xiuzhu, ZHANG Junfan, ZHU Shize, XIAO Bolv, MA Zongyi |
| 图2 用不同粒径的Al粉在不同热压温度下制备的15%SiC/2009Al复合材料热压态的OM图 |
| Fig.2 Metallographic diagrams of hot-pressed 15%SiC/2009Al composite prepared by aluminum powder with different sizes at different hot pressing temperatures (a) 13 μm/560oC, (b) 13 μm/580oC, (c) 13 μm/600oC, (d) 32 μm/560oC, (e) 32 μm/580oC, (f) 32 μm/600oC |
|
|