一种含Re/Ru镍基单晶合金的蠕变行为及其机理
Creep Behavior and Mechanism of a Re/Ru-containing Nickel-based Single Crystal Superalloy
一种含Re/Ru镍基单晶合金的蠕变行为及其机理 |
| 田淞文, 刘丽荣, 田素贵 |
|
Creep Behavior and Mechanism of a Re/Ru-containing Nickel-based Single Crystal Superalloy |
| TIAN Songwen, LIU Lirong, TIAN Sugui |
| 图8 样品在1100℃/140 MPa和1140℃/140 MPa条件下蠕变断裂后不同位置的γ′相形貌 |
| Fig.8 Microstructure in various zones of sample after crept until fracture at 1100oC/140 MPa and 1140oC/140 MPa (a) region far from fracture at 1100oC, (b) region near fracture at 1100oC, (c) region far from fracture at 1140oC and (d) region near fracture at 1140oC |
|
|