GCr15轴承钢时效过程碳化物的演化行为
刘震寰, 李勇翰, 刘洋, 王培, 李殿中

Carbide Evolution Behavior of GCr15 Bearing Steel During Aging Process
LIU Zhenhuan, LI Yonghan, LIU Yang, WANG Pei, LI Dianzhong
表3 不同晶面的衍射强度因子之比
Table 3 Ratio of diffraction intensity factors of distinct crystal planes
Diffraction crystal planes of martensiteAustenite diffraction crystallineG
(200)M(200) γ2.46
(220) γ1.32
(311) γ1.78
(211)M(200) γ1.21
(220) γ0.65
(311) γ0.87