Al基复合涂层干摩擦磨损的有限元分析

王慧明, 王金龙, 李应举, 张宏毅, 吕晓仁

Finite Element Analysis of Dry Friction Wear of Al-based Composite Coatings

WANG Huiming, WANG Jinlong, LI Yingju, ZHANG Hongyi, LV Xiaoren

表8 Al2O3含量为0%、30%、45%的Al基复合涂层的磨损量仿真值和实验数据及其差

Table 8 Simulated and experimental values of wear amount of Al-based composite coatings with Al2O3 content of 0%, 30%, and 45% and their errors

Coating Al 30% Al2O3 45% Al2O3 Simulated / mm3 0.0702 0.0195 0.0170 Experimental / mm3 0.0679 0.0190 0.0167 e / % 3.3873 2.6316 1.7964