Cr含量对Ni-Fe-Cr-Al合金抗氧化性能的影响
张凯1, 付广艳1(
), 刘恩泽2, 谭政2, 宁礼奎2, 郑志2
), 刘恩泽2, 谭政2, 宁礼奎2, 郑志2
Effect of Cr Content on Oxidation Resistance of Ni-Fe-Cr-Al Alloy
ZHANG Kai1, FU Guangyan1(), LIU Enze2, TAN Zheng2, NING Likui2, ZHENG Zhi2
), LIU Enze2, TAN Zheng2, NING Likui2, ZHENG Zhi2
图6. 20%Cr合金在1200℃氧化不同时间后的横截面EDS面扫结果
Fig.6. EDS surface scan results of 20%Cr alloy oxidized at 1200℃ for different times 1 h (a), 100 h (b)