Cr含量对Ni-Fe-Cr-Al合金抗氧化性能的影响
张凯1, 付广艳1(
), 刘恩泽2, 谭政2, 宁礼奎2, 郑志2
), 刘恩泽2, 谭政2, 宁礼奎2, 郑志2
Effect of Cr Content on Oxidation Resistance of Ni-Fe-Cr-Al Alloy
ZHANG Kai1, FU Guangyan1(), LIU Enze2, TAN Zheng2, NING Likui2, ZHENG Zhi2
), LIU Enze2, TAN Zheng2, NING Likui2, ZHENG Zhi2
图5. 三种合金在1200℃氧化不同时间后的横截面形貌
Fig.5. Cross-sectional morphology of three alloys after oxidation at 1200oC for different times (a) 1 h, 20%Cr, (b) 1 h, 24%Cr, (c) 1 h, 28%Cr, (d) 100 h, 20%Cr, (e) 100 h, 24%Cr, (f) 100 h, 28%Cr