稀土Ce对X20Co马氏体耐热钢蠕变性能的影响

向钰琳, 杨仁贤, 蔡欣, 胡小强, 李殿中

Effect of Ce Addition on Creep Properties of X20Co Martensitic Heat-resistant Steel

XIANG Yulin, YANG Renxian, CAI Xin, HU Xiaoqiang, LI Dianzhong

表1 X20Co耐热钢的化学成分

Table 1 Chemical composition of the experimental X20Co heat-resistant steels (mass fraction, %)

Steel C Si Mn Cr Co Mo W V Nb Ce Fe 0Ce 0.21 0.25 0.31 9.91 9.79 3.06 5.91 0.22 0.07 0 Bal. 5Ce 0.26 0.21 0.22 9.88 10.06 3.06 5.93 0.22 0.07 0.005 Bal. 12Ce 0.22 0.25 0.31 9.99 9.95 3.09 5.89 0.23 0.07 0.012 Bal.