定向再结晶对热轧态Cu71Al18Mn11合金的组织和超弹性性能的影响
Effects of Directional Recrystallization on Microstructure and Superelastic Property of Hot-rolled Cu71Al18Mn11 Alloy
定向再结晶对热轧态Cu71Al18Mn11合金的组织和超弹性性能的影响 |
| 徐利君, 郑策, 冯小辉, 黄秋燕, 李应举, 杨院生 |
|
Effects of Directional Recrystallization on Microstructure and Superelastic Property of Hot-rolled Cu71Al18Mn11 Alloy |
| XU Lijun, ZHENG Ce, FENG Xiaohui, HUANG Qiuyan, LI Yingju, YANG Yuansheng |
| 图13 热轧Cu71Al18Mn11合金在700℃退火30 min后的IPF图、再结晶分数和晶界分布以及在750℃退火20 min后的IPF图和晶界分布 |
| Fig.13 Inverse pole figure (a), recrystallization fraction (b) and grain boundary distribution (c) of hot rolled Cu71Al18Mn11 alloy after annealing at 700℃ for 30 min and inverse pole figure (d) and grain boundary distribution (e) after annealing at 750℃ for 20 min |
|
|