Ni(OH)2 负极材料的十二烷基硫酸钠辅助制备及其储锂性能
Lithium Ions Storage Properties of Ni(OH)2 Anode Materials Prepared with Sodium Dodecyl Sulfate as Accessory Ingredient
Ni(OH)2 负极材料的十二烷基硫酸钠辅助制备及其储锂性能 |
| 李延伟, 罗康, 姚金环 |
|
Lithium Ions Storage Properties of Ni(OH)2 Anode Materials Prepared with Sodium Dodecyl Sulfate as Accessory Ingredient |
| LI Yanwei, LUO Kang, YAO Jinhuan |
| 图5 NS-0和NS-20样品在不同扫描速度下的CV曲线、NS-20样品在0.5 mV·s-1扫描速度下的CV曲线、NS-10、NS-20和NS-30样品在不同扫描速度下的赝电容贡献百分比 |
| Fig.5 CV curves of NS-0 (a) and (b) NS-20 samples at various scan rates; CV curve of NS-20 at 0.5 mV·s-1 (the region filled with blue color corresponds to pseudocapacitive effect) (c); pseudocapacitance contribution percentage diagram of NS-10 (d), NS-20 (e) and NS-30 (f) samples at different scanning speeds |
|
|