CrTaTi难熔中熵合金的力学性能和抗氧化性能
史畅, 杜宇航, 赖利民, 肖思明, 郭宁, 郭胜锋

Mechanical Properties and Oxidation Resistance of a Refractory Medium-entropy Alloy CrTaTi
SHI Chang, DU Yuhang, LAI Liming, XIAO Siming, GUO Ning, GUO Shengfeng
表2 一些典型难熔多主元合金在1000℃氧化3 h后的增重
Table 2 Oxidation weight gain of typical refractory multi-component alloys after oxidation at 1000℃ for 3 h
Alloy compositionWeight gain /mg·cm-2Ref.Alloy compositionWeight gain /mg·cm-2Ref.
CrTaTi0.932This workAlNb1.5Ta0.5Ti1.5Zr0.510[37]
CrTaVW30[34]AlCrMoTiW3.8[38]
CrMo0.5NbTa0.5TiZr110[36]AlCr0.5Mo0.5NbTiZr21[39]
CrNbTiZr25[35]Al0.5Mo1.5NbTiZr20[39]
NbTiVZr100[35]AlCrNbTiZr39[39]
AlCrMoNbTi0.8[36]CrMoNbTaV13[40]