两种“W替Re”型低成本第二代镍基单晶高温合金的高温持久变形机制 |
|||||||||||||||
| 周章瑞, 吕培森, 赵国旗, 张剑, 赵云松, 刘丽荣 | |||||||||||||||
|
Stress Rupture Deformation Mechanism of Two "Replacement of Re by W" Type Low-cost Second-generation Nickel Based Single Crystal Superalloys at Elevated Temperatures |
|||||||||||||||
| ZHOU Zhangrui, LV Peisen, ZHAO Guoqi, ZHANG Jian, ZHAO Yunsong, LIU Lirong | |||||||||||||||
| 表3 1070℃/137 MPa下断裂后应力轴与筏形γ'相夹角统计结果 |
|||||||||||||||
| Table 3 Statistical data results of the angles between the stress axis and the rafted γ' phase after fracture at 1070℃/137 MPa |
|||||||||||||||
|
|||||||||||||||