基于内部失效机理预测评估渗碳Cr-Ni齿轮钢的超高周疲劳强度
Prediction and Evaluation of Very-high Cycle Fatigue Strength of Carburized Cr-Ni Gear Steel Based on Interior Failure Mechanism
基于内部失效机理预测评估渗碳Cr-Ni齿轮钢的超高周疲劳强度 |
| 邓海龙, 刘兵, 郭扬, 康贺铭, 李明凯, 李永平 |
|
Prediction and Evaluation of Very-high Cycle Fatigue Strength of Carburized Cr-Ni Gear Steel Based on Interior Failure Mechanism |
| DENG Hailong, LIU Bing, GUO Yang, KANG Heming, LI Mingkai, LI Yongping |
| 图6 裂纹特征尺寸与σa的关系 |
| Fig.6 Relationships between crack sizesand σa |
|
|