无取向硅钢中第二相的析出行为
|
|
徐阳, 李彦睿, 刘宝胜, 刘雯, 张少华, 卫英慧
|
Precipitation of Second Phase in Non-oriented Silicon Steel
|
|
XU Yang, LI Yanrui, LIU Baosheng, LIU Wen, ZHANG Shaohua, WEI Yinghui
|
|
表3 在不同常化温度下AlN和MnS的平衡沉淀量
|
Table 3 Equilibrium precipitation amount of the AlN and MnS at different normalization temperatures
|
|
| Precipitation temperature/℃ | Precipitation maximum amount/%, mass fraction | Precipitation equilibrium amount/%, mass fraction |
|---|
| AlN(α+γ) | 1389 | 6.20×10-3 | 6.06×10-3 (97.75%) | | AlN(α) | 1380 | 6.13×10-3 | 5.84×10-3 (95.32%) | | AlN(γ) | 1128 | 5.11×10-3 | 3.07×10-3 (60.19%) | | MnS(α+γ) | 2126 | 6.85×10-3 | 6.85×10-3 (99.89%) | | MnS(α) | 1166 | 6.56×10-3 | 5.41×10-3 (80.55%) | | MnS(γ) | 1220 | 6.55×10-3 | 5.66×10-3 (86.38%) |
|
|
|