中间相沥青基碳纤维石墨化度对Cf/Al界面损伤的影响
Effect of Graphitization Degree of Mesophase Pitch-based Carbon Fibers on Carbon Fiber/Al Interface Damage
中间相沥青基碳纤维石墨化度对Cf/Al界面损伤的影响 |
| 张鹏, 黄东, 张福全, 叶崇, 伍孝, 吴晃 |
|
Effect of Graphitization Degree of Mesophase Pitch-based Carbon Fibers on Carbon Fiber/Al Interface Damage |
| ZHANG Peng, HUANG Dong, ZHANG Fuquan, YE Chong, WU Xiao, WU Huang |
| 图9 石墨化度对界面反应活性的影响机制和拉伸断裂过程中碳纤维微观结构对裂纹扩展的影响机制 |
| Fig.9 Interfacial damage influence mechanism (a) mechanism of effect of graphitization degree on interfacial reactivity; (b) influence mechanism of carbon fiber microstructure on crack propagation during tensile fracture |
|
|