碳纤维/铝复层材料的组织和力学性能

王艳坤, 王宇, 纪伟, 王智慧, 彭翔飞, 呼宇雄, 刘斌, 徐宏, 白培康

Microstructure and Mechanical Properties of Carbon Fiber/Aluminum Laminated Composites

WANG Yankun, WANG Yu, JI Wei, WANG Zhihui, PENG Xiangfei, HU Yuxiong, LIU Bin, XU Hong, BAI Peikang

图10 630℃、100 min、21 MPa下不同纤维含量试样的三点抗弯图

Fig.10 Three point bending diagram of samples with diff-erent fiber volume fraction at 630℃, 100 min, 21 MPa (1 group-0.1 mm Al, 4-layer fibers, 2 group-0.4 mm Al, 4-layer fibers, 3 group-0.3 mm Al, 3-layer fibers)