CuO纳米阵列结构光阴极的制备及其光电化学分解水的性能
Controlled Synthesis of CuO Nanoarrays as Efficient Photocathodes for Photoelectrochemical (PEC) for Water Splitting
CuO纳米阵列结构光阴极的制备及其光电化学分解水的性能 |
| 孟祥东, 甄超, 刘岗, 成会明 |
|
Controlled Synthesis of CuO Nanoarrays as Efficient Photocathodes for Photoelectrochemical (PEC) for Water Splitting |
| MENG Xiangdong, ZHEN Chao, LIU Gang, CHENG Huiming |
| 图16 基底温度为400℃、溅射时间为90 min、制备压力分别为1.0 Pa、1.5 Pa、4.1 Pa和8.5 Pa的CuO NAs光阴极的莫特-肖特基曲线 |
| Fig.16 Mott-Schottky curves of the CuO NAs photocathodes fabricated under the condition of a sputtering time of 90 min, the substrate temperature of 300℃, pressure of 1.0 Pa, 1.5 Pa, 4.1 Pa, 8.5 Pa, respectively |
|
|