CuO纳米阵列结构光阴极的制备及其光电化学分解水的性能
Controlled Synthesis of CuO Nanoarrays as Efficient Photocathodes for Photoelectrochemical (PEC) for Water Splitting
CuO纳米阵列结构光阴极的制备及其光电化学分解水的性能 |
| 孟祥东, 甄超, 刘岗, 成会明 |
|
Controlled Synthesis of CuO Nanoarrays as Efficient Photocathodes for Photoelectrochemical (PEC) for Water Splitting |
| MENG Xiangdong, ZHEN Chao, LIU Gang, CHENG Huiming |
| 图8 基底温度为400℃,溅射时间为90 min,压力分别为1.0 Pa、1.5 Pa、4.1 Pa、8.5 Pa的CuO NAs光阴极及其截面的SEM照片 |
| Fig.8 SEM images of CuO NAs photocathodes fabricated under the condition of a substrate temperature of 400℃, sputtering time of 90 min (a~d) working pressure was 1.0 Pa, 1.5 Pa, 4.1 Pa, 8.5 Pa, respectively, (e~h) corresponding cross-section pictures, the thickness of different samples was provided |
|
|