CuO纳米阵列结构光阴极的制备及其光电化学分解水的性能
Controlled Synthesis of CuO Nanoarrays as Efficient Photocathodes for Photoelectrochemical (PEC) for Water Splitting
CuO纳米阵列结构光阴极的制备及其光电化学分解水的性能 |
| 孟祥东, 甄超, 刘岗, 成会明 |
|
Controlled Synthesis of CuO Nanoarrays as Efficient Photocathodes for Photoelectrochemical (PEC) for Water Splitting |
| MENG Xiangdong, ZHEN Chao, LIU Gang, CHENG Huiming |
| 图6 压力为1.0 Pa、基底温度为300℃、溅射时间分别为15 min、30 min、60 min、90 min、120 min的CuO NAs光阴极及其截面的SEM照片 |
| Fig.6 SEM images of CuO NAs photocathodes fabricated under the condition of a pressure of 1.0 Pa and the substrate temperature of 300℃ (a~e) the samples of different sputtering time, 15 min, 30 min, 60 min, 90 min, 120 min, respectively and (f~j) corresponding cross-section pictures, the thickness of different samples was provided |
|
|