在900℃添加CeO2 对SiO2-Al2O3-ZnO-CaO搪瓷析晶和热震行为的影响 |
丰敏, 廖依敏, 陈明辉, 朱圣龙, 王福会 |
Crystallization and Thermal Shock Behaviors of SiO2-Al2O3-ZnO-CaO-based Glass with Added Different Contents of CeO2 at 900℃ |
FENG Min, LIAO Yimin, CHEN Minghui, ZHU Shenglong, WANG Fuhui |
图10 E10C、E15C和E20C搪瓷涂层在900℃热震30次后截面微观形貌 |
Fig.10 Cross-sectional microstructures of E10 C (a), E15C (b) and E20C (c) enamel coatings after thermal shock for 30 cyc at 900℃ (Inset in Fig.10b shows the local enlarged image) |
![]() |