在900℃添加CeO2 对SiO2-Al2O3-ZnO-CaO搪瓷析晶和热震行为的影响
Crystallization and Thermal Shock Behaviors of SiO2-Al2O3-ZnO-CaO-based Glass with Added Different Contents of CeO2 at 900℃
在900℃添加CeO2 对SiO2-Al2O3-ZnO-CaO搪瓷析晶和热震行为的影响 |
| 丰敏, 廖依敏, 陈明辉, 朱圣龙, 王福会 |
|
Crystallization and Thermal Shock Behaviors of SiO2-Al2O3-ZnO-CaO-based Glass with Added Different Contents of CeO2 at 900℃ |
| FENG Min, LIAO Yimin, CHEN Minghui, ZHU Shenglong, WANG Fuhui |
| 图8 涂覆有E10C、E15C和E20C搪瓷涂层的样品在900℃的热震动力学曲线 |
| Fig.8 Mass change of specimens with E10C, E15C, and E20C enamel coatings after thermal shock at 900℃ for different cycles |
|
|