在900℃添加CeO2 对SiO2-Al2O3-ZnO-CaO搪瓷析晶和热震行为的影响
Crystallization and Thermal Shock Behaviors of SiO2-Al2O3-ZnO-CaO-based Glass with Added Different Contents of CeO2 at 900℃
在900℃添加CeO2 对SiO2-Al2O3-ZnO-CaO搪瓷析晶和热震行为的影响 |
| 丰敏, 廖依敏, 陈明辉, 朱圣龙, 王福会 |
|
Crystallization and Thermal Shock Behaviors of SiO2-Al2O3-ZnO-CaO-based Glass with Added Different Contents of CeO2 at 900℃ |
| FENG Min, LIAO Yimin, CHEN Minghui, ZHU Shenglong, WANG Fuhui |
| 图7 E20C在900℃晶化0.5 h后的TEM微观结构和元素分布 |
| Fig.7 TEM microstructure and elemental mapping of E20C annealed at 900℃ for 0.5 h |
|
|